大连SA738GrE/SA738GrE/SA738GrE-40度冲击/SA738GrE压力容器
二、SA738GrE力学性能
SA738GrE力学性能要求,
|
抗拉强度，Ksi(MPa) |
||||
|
≤1.5in(40mm)
|
＞1.5in(40mm)~2.0in(50mm)
|
＞2.0in(50mm)~2.5in(65mm)
|
＞2.0in.(65mm)~4in.(100mm)
|
＞4in.(100mm)
|
|
90~110 (620~760) |
90~110 (620~760) |
1 |
1 |
1 |
|
屈服强度：Ksi(MPa): |
||||
|
≤1.5in(40mm)
|
＞1.5in(40mm)~2.0in(50mm)
|
＞2.0in(50mm)~2.5in(65mm)
|
＞2.0in.(65mm)~4in.(100mm)
|
＞4in.(100mm)
|
|
75(515) |
75(515) |
1 |
1 |
1 |
|
标距2In.(50mm)伸长率，%≥ |
||||
|
≤1.5in(40mm)
|
＞1.5in(40mm)~4.0in(100mm)
|
＞4in.(100mm)
|
||
|
20 |
1 |
1 |
||
注：t=钢板的公称厚度。
二、SA738GrE交货状态
SA738GBr钢板的交货状态应为调质（淬火加回火）处理。SA738B钢板回火处理温度为1100°F（595℃）。
SA738GrE,属于中、低温压力容器用热处理的碳锰硅钢板。 SA738GrE也属于镇静钢。SA738GrE钢板按极限抗拉强度有78Ksi(515MPa),85Ksi(585MPa),80Ksi(550Mpa)和90Ksi(620MPa)四个级别。 SA738GrE厚度为4in(40mm)和2in.(50mm)。SA738GrE执行标准：ASME SA738/SA738M。
二、SA738GrE化学成分
SA738B化学成分要求
元素名称
成分%
E级
C1
≤0.122
Mn
熔
炼
分
析
≤1.5in(40mm)
0.10~1.602
＞1.5~2.0in(40-50mm)
0.10~1.602
＞2.0~2.5in(50~65mm)
3
＞2.5in(65mm)
3
成
品
分
析
≤1.5in(40mm)
1.02~1.722
＞1.5~2.0in(40-50mm)
1.02~1.722
＞2.0~2.5in(50~65mm)
3
＞2.5in(65mm)
3
P1
≤0.015
S1
≤0.006
Si
熔炼分析
0.15~0.50
成品分析
0.13~0.55
Cu
熔炼分析
≤0.35
成品分析
≤0.38
Ni
熔炼分析
≤0.70
成品分析
≤0.73
Cr
熔炼分析
≤0.30
成品分析
≤0.34
Mo
熔炼
分析
≤1.5in(40mm)
≤0.35
＞1.5（40mm)
3
成品
分析
≤1.5in(40mm)
≤0.38
＞1.5（40mm)
3
V
熔炼分析
≤0.09
成品分析
≤0.10
Nb
熔炼分析
≤0.05
成品分析
≤0.06
Nb+V
熔炼分析
≤0.12
成品分析
≤0.13
Ti1
7
B1
0.0007
AL1
总量≤0.020或酸溶铝≤0.0157
注：1.熔炼分析与成品分析都适用。
2.不允许。
7.根据钢板厂与采购方的协议钢中可加入钛（Ti),这种情况下含量不再适用。如运用这一选择时，钛的熔炼分析含量为0.006%至小于等于0.03%，且钛含量的熔炼和成品分析结果须在试验报告中报告之。
二、SA738GrE应用
SA738GrE河南昌申钢铁有限公司，舞钢钢厂 70吨起订，主要用于容器承压件，和压力容器用钢板。核电站用钢制作安全壳.钢制安全壳的母材和设备闸门插入板.SA738GrE常用于核电工程上核岛级钢板。
、SA738GrE简介
SA738GrE,属于中、低温压力容器用热处理的碳锰硅钢板。 SA738GrE也属于镇静钢。SA738GrE钢板按极限抗拉强度有78Ksi(515MPa),85Ksi(585MPa),80Ksi(550Mpa)和90Ksi(620MPa)四个级别。 SA738GrE厚度为4in(40mm)和2in.(50mm)。SA738GrE执行标准：ASME SA738/SA738M。