美国SABIC LEXAN PC DMX1214是一种改进流程，改进的耐划伤透明copolycarbonate树脂
SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D 792 |
| 密度 | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| 1.17 g/cc | 0.0423 lb/in³ | ASTM D 792 | |
| 吸水率 |
0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ASTM D 570 |
| 平衡吸湿 | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 |
| 0.14 % | 0.14 % | 50% RH; ASTM D 570 | |
|
0.30 %
@Temperature 23.0 °C
|
0.30 %
@Temperature 73.4 °F
|
ASTM D 570 | |
|
0.050 %
@Time 86400 sec
|
0.050 %
@Time 24.0 hour
|
50% RH; ASTM D 570 | |
| 饱和吸水率 |
0.30 %
@Temperature 23.0 °C
|
0.30 %
@Temperature 73.4 °F
|
ISO 62 |
| 线性成型收缩率,Flow |
0.0050 - 0.0080 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0080 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 |
16 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
16 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
|
17.1 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
17.1 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗张强度(屈服) | 77.0 MPa | 11200 psi | Type I, 50 mm/min; ASTM D 638 |
| 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 60 % | 60 % | 50 mm/min; ISO 527 |
| 92 % | 92 % | Type I, 50 mm/min; ASTM D 638 | |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 |
| 8.0 % | 8.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 |
| 2.83 GPa | 410 ksi | 50 mm/min; ASTM D 638 | |
| 弯曲强度 | 101 MPa | 14600 psi | 2 mm/min; ISO 178 |
| 116 MPa | 16800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 弯曲模量 | 2.31 GPa | 335 ksi | 2 mm/min; ISO 178 |
| 2.63 GPa | 381 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 |
0.320 J/cm
@Temperature -30.0 °C
|
0.599 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
|
0.370 J/cm
@Temperature 23.0 °C
|
0.693 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| 悬壁梁无缺口冲击强度 |
NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ASTM D 4812 |
| 悬壁梁缺口冲击强度 |
4.00 kJ/m²
@Temperature -30.0 °C
|
1.90 ft-lb/in²
@Temperature -22.0 °F
|
80*10*3; ISO 180/1A |
|
6.00 kJ/m²
@Temperature 23.0 °C
|
2.86 ft-lb/in²
@Temperature 73.4 °F
|
80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 |
93.0 kJ/m²
@Temperature -30.0 °C
|
44.3 ft-lb/in²
@Temperature -22.0 °F
|
80*10*3; ISO 180/1U |
|
NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 |
13.3 J/cm²
@Temperature -30.0 °C
|
63.3 ft-lb/in²
@Temperature -22.0 °F
|
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
|
NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 |
0.300 J/cm²
@Temperature -30.0 °C
|
1.43 ft-lb/in²
@Temperature -22.0 °F
|
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
|
0.300 J/cm²
@Temperature 23.0 °C
|
1.43 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 |
68.0 J
@Temperature 23.0 °C
|
50.2 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 |
60.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
|
33.3 µin/in-°F
@Temperature 73.4 - 176 °F
|
ISO 11359-2 |
|
60.0 µm/m-°C
@Temperature -40.0 - 95.0 °C
|
33.3 µin/in-°F
@Temperature -40.0 - 203 °F
|
ASTM E 831 | |
| 线性热膨胀系数,横向流动 |
60.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
|
33.3 µin/in-°F
@Temperature 73.4 - 176 °F
|
ISO 11359-2 |
|
60.0 µm/m-°C
@Temperature -40.0 - 95.0 °C
|
33.3 µin/in-°F
@Temperature -40.0 - 203 °F
|
ASTM E 831 | |
| 载荷下热变形温度(0.46 MPa) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
133 °C
@Thickness 3.20 mm
|
271 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
121 °C
@Thickness 3.20 mm
|
250 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 维卡软化温度 | 138 °C | 280 °F | Rate B/50; ASTM D 1525 |
| 141 °C | 286 °F | Rate B/50; ISO 306 | |
| 142 °C | 288 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) |
HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.584 | 1.584 | ASTM D 542 |
| 1.584 | 1.584 | ISO 489 | |
| 雾度 |
<= 0.80 %
@Thickness 2.54 mm
|
<= 0.80 %
@Thickness 0.100 in
|
ASTM D 1003 |
| Transmission, Visible |
88 %
@Thickness 2.54 mm
|
88 %
@Thickness 0.100 in
|
ASTM D 1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 球压试验，125°C+/-2℃ | Pass | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | F | ASTM D 3363 |