产品详情
美国SABIC LEXAN PC DMX6014是射出成形电脑共聚物ABS混合物。这种树脂结合良好的抗划伤性和延展性
SABIC Innovative Plastics Lexan® DMX6014 PC Copolymer (Asia Pacific) 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.15 g/cc | 1.15 g/cc | ASTM D 792 |
| 密度 | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| 线性成型收缩率,Flow |
0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 |
10 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
10 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
|
12 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
12 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hardness, Rockwell L | 90 | 90 | ASTM D 785 |
| 洛氏硬度（R 级） | 117 | 117 | ASTM D 785 |
| 抗张强度(断裂) | 45.0 MPa | 6530 psi | Type I, 50 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D 638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | 45 % | 45 % | Type I, 50 mm/min; ASTM D 638 |
| 50 % | 50 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 5.5 % | 5.5 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.15 GPa | 312 ksi | 1 mm/min; ISO 527 |
| 2.40 GPa | 348 ksi | 5 mm/min; ASTM D 638 | |
| 弯曲强度 | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 78.0 MPa | 11300 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 |
| 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| 悬壁梁缺口冲击强度 |
0.700 J/cm
@Temperature -30.0 °C
|
1.31 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
|
2.20 J/cm
@Temperature 23.0 °C
|
4.12 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
|
10.0 kJ/m²
@Temperature -30.0 °C
|
4.76 ft-lb/in²
@Temperature -22.0 °F
|
80*10*3; ISO 180/1A | |
|
20.0 kJ/m²
@Temperature 23.0 °C
|
9.52 ft-lb/in²
@Temperature 73.4 °F
|
80*10*3; ISO 180/1A | |
| 简支梁缺口冲击强度 |
1.00 J/cm²
@Temperature -30.0 °C
|
4.76 ft-lb/in²
@Temperature -22.0 °F
|
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
|
2.00 J/cm²
@Temperature 23.0 °C
|
9.52 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 55.0 J | 40.6 ft-lb | Multiaxial Impact; ISO 6603 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电常数 |
2.8
@Frequency 1.00e+6 Hz
|
2.8
@Frequency 1.00e+6 Hz
|
IEC 60250 |
|
3.0
@Frequency 50.0 - 60.0 Hz
|
3.0
@Frequency 50.0 - 60.0 Hz
|
IEC 60250 | |
|
3.0
@Frequency 1000 Hz
|
3.0
@Frequency 1000 Hz
|
IEC 60250 | |
| 介电强度 |
35.0 kV/mm
@Thickness 1.60 mm
|
889 kV/in
@Thickness 0.0630 in
|
in oil; IEC 60243-1 |
|
47.0 kV/mm
@Thickness 0.800 mm
|
1190 kV/in
@Thickness 0.0315 in
|
in oil; IEC 60243-1 | |
| 耗散因数 |
0.010
@Frequency 1.00e+6 Hz
|
0.010
@Frequency 1.00e+6 Hz
|
IEC 60250 |
|
0.012
@Frequency 1000 Hz
|
0.012
@Frequency 1000 Hz
|
IEC 60250 | |
|
0.030
@Frequency 50.0 - 60.0 Hz
|
0.030
@Frequency 50.0 - 60.0 Hz
|
IEC 60250 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hot Ball Pressure Test | <= 100 °C | <= 212 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 113 °C | 235 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
113 °C
@Thickness 3.20 mm
|
235 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 载荷下热变形温度(1.8 MPa) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
97.0 °C
@Thickness 3.20 mm
|
207 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| 维卡软化温度 | 113 °C | 235 °F | Rate B/50; ASTM D 1525 |
| 113 °C | 235 °F | Rate B/50; ISO 306 | |
| 118 °C | 244 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) |
HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
UL 94 |
|
HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
2nd value; UL 94 | |
| 灼热丝易燃指数 |
650 °C
@Thickness 1.50 mm
|
1200 °F
@Thickness 0.0591 in
|
Glow Wire Flammability Index; IEC 60695-2-12 |
|
700 °C
@Thickness 3.00 mm
|
1290 °F
@Thickness 0.118 in
|
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | pass | IEC 60695-10-2 |
| Erichson scratch depth, 6N, micrometer | 14 | SABIC Method |
| Pencil Hardness test, 1kgf | F | ASTM D 3363 |