产品详情
美国SABIC LEXAN PC EXL1132是一种高流动性，紫外线稳定，注塑级
| General | ||||
|
Material Status
|
|
|||
|
UL Yellow Card 1
|
||||
|
Search for UL Yellow Card
|
||||
|
Availability
|
|
|||
|
Uses
|
|
|||
|
RoHS Compliance
|
|
|||
|
Also Available In
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
|||
|
--
|
1.18
|
g/cm³
|
ASTM D792 |
|
--
|
1.19
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)
|
17
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)
|
16
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
Internal Method | ||
|
Across Flow : 3.20 mm
|
0.40 to 0.80
|
%
|
|
|
Flow : 3.20 mm
|
0.40 to 0.80
|
%
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 23°C
|
0.35
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
0.15
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Ball Indentation Hardness (H 358/30)
|
95.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
-- 2
|
2280
|
MPa
|
ASTM D638 |
|
--
|
2150
|
MPa
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield 3
|
58.0
|
MPa
|
ASTM D638 |
|
Yield
|
57.0
|
MPa
|
ISO 527-2/50 |
|
Break 3
|
58.0
|
MPa
|
ASTM D638 |
|
Break
|
55.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Elongation
|
|||
|
Yield 3
|
5.8
|
%
|
ASTM D638 |
|
Yield
|
5.0
|
%
|
ISO 527-2/50 |
|
Break 3
|
110
|
%
|
ASTM D638 |
|
Break
|
100
|
%
|
ISO 527-2/50 |
|
Flexural Modulus
|
|||
|
50.0 mm Span 4
|
2320
|
MPa
|
ASTM D790 |
|
-- 5
|
2240
|
MPa
|
ISO 178 |
|
Flexural Stress
|
|||
|
-- 5, 6
|
85.0
|
MPa
|
ISO 178 |
|
Yield, 50.0 mm Span 4
|
95.0
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength 7
|
ISO 179/1eA | ||
|
-30°C
|
25
|
kJ/m²
|
|
|
23°C
|
60
|
kJ/m²
|
|
|
Charpy Unnotched Impact Strength 7
|
ISO 179/1eU | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
|
Notched Izod Impact
|
|||
|
-30°C
|
670
|
J/m
|
ASTM D256 |
|
23°C
|
750
|
J/m
|
ASTM D256 |
|
-30°C 8
|
20
|
kJ/m²
|
ISO 180/1A |
|
23°C 8
|
55
|
kJ/m²
|
ISO 180/1A |
|
Unnotched Izod Impact Strength 8
|
ISO 180/1U | ||
|
-30°C
|
No Break
|
|
|
|
23°C
|
No Break
|
|
|
|
Instrumented Dart Impact (23°C, Total Energy)
|
69.0
|
J
|
ASTM D3763 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed, 3.20 mm
|
136
|
°C
|
ASTM D648 |
|
0.45 MPa, Annealed 9
|
136
|
°C
|
ISO 75-2/Be |
|
1.8 MPa, Unannealed, 3.20 mm
|
123
|
°C
|
ASTM D648 |
|
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 10
|
125
|
°C
|
ISO 75-2/Ae |
|
Vicat Softening Temperature
|
|||
|
--
|
144
|
°C
|
ASTM D1525 11, ISO 306/B50 11 |
|
--
|
145
|
°C
|
ISO 306/B120 |
|
Ball Pressure Test (123 to 127°C)
|
Pass
|
|
IEC 60695-10-2 |
|
CLTE
|
|||
|
Flow : -40 to 40°C
|
7.2E-5
|
cm/cm/°C
|
ASTM E831 |
|
Flow : 23 to 80°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
Transverse : -40 to 40°C
|
7.6E-5
|
cm/cm/°C
|
ASTM E831 |
|
Transverse : 23 to 80°C
|
7.5E-5
|
cm/cm/°C
|
ISO 11359-2 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
120
|
°C
|
UL 746 |
|
RTI Str
|
125
|
°C
|
UL 746 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Glow Wire Flammability Index
|
IEC 60695-2-12 | ||
|
1.0 mm
|
850
|
°C
|
|
|
3.0 mm
|
960
|
°C
|
|
|
Glow Wire Ignition Temperature
|
IEC 60695-2-13 | ||
|
1.0 mm
|
875
|
°C
|
|
|
3.0 mm
|
875
|
°C
|
|
|
Oxygen Index
|
32
|
%
|
ISO 4589-2 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
120
|
°C
|
|
|
Drying Time
|
3.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Suggested Shot Size
|
40 to 60
|
%
|
|
|
Rear Temperature
|
270 to 295
|
°C
|
|
|
Middle Temperature
|
280 to 305
|
°C
|
|
|
Front Temperature
|
295 to 315
|
°C
|
|
|
Nozzle Temperature
|
290 to 310
|
°C
|
|
|
Processing (Melt) Temp
|
295 to 315
|
°C
|
|
|
Mold Temperature
|
70 to 95
|
°C
|
|
|
Back Pressure
|
0.300 to 0.700
|
MPa
|
|
|
Screw Speed
|
40 to 70
|
rpm
|
|
|
Vent Depth
|
0.025 to 0.076
|
mm
|