牌号
|
1.4941压力容器用不锈钢扁平
|
|
|
|
|
|
|
|
|
|
|
X6CrNiTiB18-10
|
|
|
|
|
|
|
|
|
|
对应标准
|
NF EN 10028-7-2008
|
|
|
|
|
|
|
|
|
|
压力容器用不锈钢扁平产品
|
|
|
|
|
|
|
|
|
|
Flat products made of steels for pressure purposes - Part 7 : stainless steels
|
|
|
|
|
|
|
|
|
|
归类
|
奥氏体不锈钢
|
|
|
|
|
|
|
|
|
|
标签
|
抗蠕变等级
|
|
|
|
|
|
|
|
|
|
X6CrNiTiB18-10 化学元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
B
|
更多
|
|
ZUI小值
|
0.04
|
-
|
-
|
-
|
-
|
17
|
9
|
0.0015
|
Ti:5×C~0.8
|
|
ZUI大值
|
0.08
|
1
|
2
|
0.035
|
0.015
|
19
|
12
|
0.005
|
|
◎ 未经买方同意，不得随意向钢中添加表中未列的元素，冶炼精加工除外。采取一切必要措施以防在废钢和生产原料中带入这些元素，因为其会削弱钢的机械性能，降低钢的适用性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
X6CrNiTiB18-10 机械性能
|
|
|
|
|
|
|
|
|
|
|
条件
|
热处理或状态
|
抗拉强度
|
屈服点
|
断后伸长率或延伸率
|
冲击吸收能量
|
|
|
|
|
|
σb
|
σs
|
δ
|
KV2
|
|
|
|
|
|
Mpa
|
Mpa
|
%
|
J
|
|
|
|
|
|
C：T ≤ 8
|
+AT
|
510~710
|
Rp0.2：≥220
|
T ＜ 3mm: ≥40
|
20℃：
|
|
|
|
|
|
Rp1.0：≥250
|
T ≥ 3mm: ≥ 40
|
(l: ≥100；t: ≥60)
|
|
|
|
|
|
①②
|
②③
|
|
|
|
|
|
|
H：T ≤ 13.5
|
+AT
|
510~710
|
Rp0.2：≥200
|
T ＜ 3mm: ≥40
|
20℃：
|
|
|
|
|
|
Rp1.0：≥240
|
T ≥ 3mm: ≥ 40
|
(l: ≥100；t: ≥60)
|
|
|
|
|
|
①②
|
②③
|
|
|
|
|
|
|
P：T ≤ 75
|
+AT
|
490~690
|
Rp0.2：≥200
|
T ＜ 3mm: ≥40
|
20℃：
|
|
|
|
|
|
Rp1.0：≥240
|
T ≥ 3mm: ≥ 40
|
(l: ≥100；t: ≥60)
|
|
|
|
|
|
①②
|
②③
|
|
|
|
|
|
|
◎C- 冷轧带钢; H- 热轧带钢; P- 热轧中厚板；T- 厚度；t- 横向；l-纵向。
|
|
|
|
|
|
|
|
|
|
|
◎+A=软化退火；+AT=固溶退火；+QT=淬火及回火；+RA=再结晶退火。
|
|
|
|
|
|
|
|
|
|
|
◎ 奥氏体钢有足够的韧性，不需要进行冲击试验。相比之下，奥氏体-铁素体钢必须按要求做冲击试验，以确保足够的韧性。
|
|
|
|
|
|
|
|
|
|
|
*抗晶间腐蚀根据EN ISO 3651-2进行测试。在交货条件下：有；在致敏状态下：有。
|
|
|
|
|
|
|
|
|
|
|
① 对于连续热轧产品，可在询价和订购时商定Rp0.2(即表中σs)的ZUI小值提高20MPa，Rp1.0的ZUI小值提高10MPa。
|
|
|
|
|
|
|
|
|
|
|
② 如果在轧制宽度<300mm的带材情况下，采用纵向试验件，ZUI小值减小如下:屈服强度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
|
|
|
|
|
|
|
|
|
|
|
③ T＜3mm：该值适用于标距为80mm、宽度为20mm的试件，也可以使用标距为50mm、宽度为12.5mm的试件。T ≥3mm：该值适用于标距为5.65√S的试件。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|