Lexan PC 920A物性表
低粘度注射成形，阻燃的PC 。特殊的表面外观。有透明和不透明的颜色。
Low viscosity injection moldable, flame retardant PC. Exceptional surface appearance. Clear, tints and opaque colors.
|
Property/特性
|
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL/机械性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
|
55
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
|
90
|
%
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
91
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
2240
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 M
|
70
|
–
|
ASTM D 785
|
|
Hardness，Rockwell / 洛氏硬度 R
|
118
|
–
|
ASTM D 785
|
|
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
IMPACT/冲击性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C
|
3204
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
640
|
J/m
|
ASTM D 256
|
|
Tensile Impact Type / 拉伸冲击值，类型”S”
|
525
|
kJ/m2
|
ASTM D 1822
|
|
Falling Dart Impact / 落锤冲击 (D 3029), 23°C
|
169
|
J
|
ASTM D 3029
|
|
THERMAL/热性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
151
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
132
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 95°C, flow（流动）
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity / 导热系数
|
0.19
|
W/m-°C
|
ASTM C 177
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Specific Gravity / 比重
|
1.21
|
–
|
ASTM D 792
|
|
Specific Volume / 比容
|
0.83
|
cm3/g
|
ASTM D 792
|
|
Density / 密度
|
1.217
|
g/cm3
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption，equilibrium / 吸水率，平衡, 100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
14.5
|
g/10 min
|
ASTM D 1238
|
|
OPTICAL/光学性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Light Transmission / 透光率
|
85
|
%
|
ASTM D 1003
|
|
Haze / 雾度
|
1
|
%
|
ASTM D 1003
|
|
Refractive Index / 折射指数
|
1.586
|
–
|
ASTM D 542
|
|
ELECTRICAL/电气性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Volume Resistivity / 体积电阻率
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air / 介电强度，空气中, 3.2 mm
|
16.7
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相对介电常数, 50/60 Hz
|
3.01
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相对介电常数, 1 MHz
|
2.96
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.0009
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.01
|
–
|
ASTM D 150
|
|
Arc Resistance, Tungsten / 耐电弧性 {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值 | Unit/单位 | Standard/标准 |
|
UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)
|
1.47
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)
|
2.99
|
mm
|
UL 94
|
|
Radiant Panel Listing / 辐射板清单
|
YES
|
–
|
UL Tested
|
|
Processing/加工方法
|
| Parameter | ||
|
Injection Molding/注塑参数
|
Value/值 | Unit/单位 |
|
Drying Temperature / 干燥温度
|
120
|
°C
|
|
Drying Time / 干燥时间
|
3 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥时间（累积的）
|
48
|
hrs
|
|
Maximum Moisture Content / 最大含湿量
|
0.02
|
%
|
|
Melt Temperature / 熔体温度
|
290 – 310
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
280 – 305
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
290 – 310
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
275 – 300
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
265 – 290
|
°C
|
|
Mold Temperature / 模具温度
|
70 – 95
|
°C
|
|
Back Pressure / 背压
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺杆速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
|
40 – 60
|
%
|
|
Vent Depth / 排气孔深度
|
0.025 – 0.076
|
mm
|
沙比特塑料贸易（苏州）有限公司是一家专业从事SABIC(即沙伯基础创新塑料公司)工程塑料进出口业务的贸易型公司。经营产品有Lexan(PC，聚碳酸酯)、Noryl(PPO,改性聚苯醚)、Valox(PBT,聚对苯二甲酸丁二酯)、Cycoloy(PC/ABS，PC与ABS合金)、Xenoy(PC/PBT)、Xylex(PC/PET)、Ultem(PEI,聚醚酰亚胺)等工程塑料。同时为广大客户提供相关塑料原料FDA证明、UL证书及COC报告。
沙比特塑料贸易（苏州）有限公司不仅是长三角地区专业的沙伯基础创新公司工程塑料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之材料，进而协助客户提高产品竟争力。
把一流的产品，以一流的服务带给客户是沙比特的经营宗旨。愿与各方宾客合作双赢，共创美好未来。’