Lexan PC 955A物性表
Lexan 955A resin 是一种聚碳酸酯（PC）产品，它可以通过注射成型进行处理。
特性包括：
阻燃/额定火焰
无卤素”
Lexan* 955A Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating. Lexan 955A resin is available in transparent and tinted color options and is a general-purpose resin that is an excellent candidate for a wide variety of applications.
|
Property/特性
|
| TYPICAL PROPERTIES (1) | |||
|
MECHANICAL/机械性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
|
67
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
|
125
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 50 mm/min
|
2270
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
101
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
2370
|
MPa
|
ASTM D 790
|
|
IMPACT/冲击性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
801
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
|
79
|
J
|
ASTM D 3763
|
|
THERMAL/热性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
143
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
126
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）
|
6.84E-05
|
1/°C
|
ASTM E 831
|
|
CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）
|
7.38E-05
|
1/°C
|
ASTM E 831
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
130
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Specific Gravity / 比重
|
1.19
|
–
|
ASTM D 792
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.6 – 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
7
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL/电气性能
|
Value/值 | Unit/单位 | Standard/标准 |
|
Arc Resistance, Tungsten / 耐电弧性 {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值 | Unit/单位 | Standard/标准 |
|
UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)
|
0.8
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)
|
3.04
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm
|
875
|
°C
|
IEC 60695-2-13
|
|
Processing/加工方法
|
| Parameter | ||
|
Injection Molding/注塑参数
|
Value/值 | Unit/单位 |
|
Drying Temperature / 干燥温度
|
120
|
°C
|
|
Drying Time / 干燥时间
|
2 – 4
|
hrs
|
|
Maximum Moisture Content / 最大含湿量
|
0.02
|
%
|
|
Melt Temperature / 熔体温度
|
290 – 320
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
280 – 310
|
°C
|
|
Front – Zone 3 Temperature / 前区3温度
|
290 – 320
|
°C
|
|
Middle – Zone 2 Temperature / 中区2温度
|
280 – 310
|
°C
|
|
Rear – Zone 1 Temperature / 后区1温度
|
270 – 300
|
°C
|
|
Hopper Temperature / 料筒温度
|
60 – 80
|
°C
|
|
Mold Temperature / 模具温度
|
80 – 120
|
°C
|
沙比特塑料贸易（苏州）有限公司是一家专业从事SABIC(即沙伯基础创新塑料公司)工程塑料进出口业务的贸易型公司。经营产品有Lexan(PC，聚碳酸酯)、Noryl(PPO,改性聚苯醚)、Valox(PBT,聚对苯二甲酸丁二酯)、Cycoloy(PC/ABS，PC与ABS合金)、Xenoy(PC/PBT)、Xylex(PC/PET)、Ultem(PEI,聚醚酰亚胺)等工程塑料。同时为广大客户提供相关塑料原料FDA证明、UL证书及COC报告。
沙比特塑料贸易（苏州）有限公司不仅是长三角地区专业的沙伯基础创新公司工程塑料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之材料，进而协助客户提高产品竟争力。
把一流的产品，以一流的服务带给客户是沙比特的经营宗旨。愿与各方宾客合作双赢，共创美好未来。