| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | Equilibrium at 50%rh; ISO 62 |
| Linear Mold Shrinkage |
0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse |
0.017 cm/cm @Thickness 2.00 mm |
0.017 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2 |
| Elongation at Yield | 25 % | 25 % | ISO 527-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ISO 527-2 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
Izod Impact, Notched (ISO) 
|
7.00 kJ/m2 @Temperature -30.0 °C |
3.33 ft-lb/in2 @Temperature -22.0 °F |
ISO 180 |
其他型号参数与生产商——————————
PA6 (polycaprolactam # nylon 6) /UGN16080MF/ Korea koplar
Use: other
Features note: GF60 high rigidity, surface improvement
Important beters: density: 1.72 g/cm3 water absorption: 0.8% molding shrinkage rate: 0.1% tensile strength: MPa bending strength: 3100 MPa bending modulus: 165000 MPa hardness: 122 hot debation temperature: 218 C
Manufacturer: South Korea koplar Engineering Plastics Co. Ltd.
PA6 (polycaprolactam # nylon 6) /GF15 FR-N/ TPC
Use: other
Important beters: density: 1.26 g/cm3 absorption rate: 1.4% molding shrinkage rate: 0.7% notched impact strength: 53.4 tensile strength: 96.5 MPa elongation: 4% bending strength: 145 MPa flexural modulus: 3100 MPa hardness: 120 thermal debation temperature: 196 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF25 L BK/ TPC
Use: other
Characteristic notes: granular materials
Important beters: density: 1.23 g/cm3 absorption rate: 0.9% molding shrinkage rate: 0.5% notched impact strength: 69.4 tensile strength: 191 MPa elongation: 3% bending strength: 290 MPa flexural modulus: 10300 MPa hardness: 115 thermal debation temperature: 213 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /E HS N/ TPC
Use: other
Features note: stability, nub
Important beters: density: 1.13 g/cm3 absorption rate: 1.6% molding shrinkage rate: 1.2% notched impact strength: 133 tensile strength: 80 MPa elongation: 90% bending strength: 117 MPa flexural modulus: 3100 MPa hardness: 100 thermal debation temperature: 76.7 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GB15 L BK/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.24 g/cm3 absorption rate: 1.1% molding shrinkage rate: 1.7% notched impact strength: 37.4 tensile strength: 68.9 MPa elongation: 3.5% bending strength: 276 MPa flexural modulus: 12600 MPa hardness: 119 thermal debation temperature: 138 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF20 L BK001/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.3 g/cm3 absorption rate: 1.4% molding shrinkage rate: 0.4% notched impact strength: 74.7 tensile strength: 131 MPa elongation: 3.5% bending strength: 200 MPa flexural modulus: 6890 MPa hardness: 115 thermal debation temperature: 204 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L BK001/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L NAT024/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L RD041/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L RD079/ TPC
Use: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company