| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer # /VS420/ Hyundai)
Usage: other
Important beters: melt flow rate: 2 g/10min density: tensile strength of 0.945 MPa: elongation at break of 21.56 g/cm3: bending modulus: 27.4 MPa hardness: VEKA softening point: 56 degrees of brittleness temperature: -65
Manufacturer: Korea Hyundai Petrochemical Company
EVA (ethylene vinyl acetate copolymer #) /1403/ America flintcomb ash
Purpose: thin film
Features: high definition, good toughness and elasticity
Important beters: melt flow rate: 1.3 g/10min density: tensile strength of 0.928 MPa: elongation at break of 16 g/cm3: hardness of 800%: VEKA softening point: 90
Manufacturer: American flint Hill resources
EVA (ethylene vinyl acetate copolymer #) /V6110M/ Yangzi BASF
Usage: other
Important beters: melt flow rate: 5.9 g/10min
Manufacturer: Yangzi Petrochemical BASF Co., Ltd.
EVA (ethylene vinyl acetate copolymer #) /V5110K/ Yangzi BASF
Usage: other
Important beters: melt flow rate: 3.6 g/10min
Manufacturer: Yangzi Petrochemical BASF Co., Ltd.
EVA (ethylene vinyl acetate copolymer # /UE635000/ Leander Basil)
Usage: other
Important beters: melt flow rate: 10 g/10min density: VEKA g/cm3 softening point: 73
Manufacturer: Leander Basel Industrial Company
EVA (ethylene vinyl acetate copolymer #) /3135XA/ DuPont dow
Purpose: hot melt
Features: heat stabilizer: BHT antioxidant
Important beters: melt flow rate: 0.35 g/10min density: VEKA g/cm3 softening point: 77
Manufacturer: Dow DuPont Co
EVA (ethylene vinyl acetate copolymer #) /3165SB/ DuPont dow
Purpose: hot melt
Note: the characteristics of additives: smoothing agent, agent, stabilizer
Important beters: melt flow rate: 0.7 g/10min density: VEKA g/cm3 softening point: 67
Manufacturer: Dow DuPont Co
EVA (ethylene vinyl acetate copolymer #) /CF-250 A/ MDI
Usage: other
Features: good flexibility
Important beters: melt flow rate: 7 g/10min density: 1.1 g/cm3 tensile strength: 10.3 MPa elongation: 250%
Manufacturer: American MDI company
EVA (ethylene vinyl acetate copolymer #) /2803A/ America Serra nice
Usage: other
Features: antioxidant
Important beters: melt flow rate: 3 g/10min density: tensile strength of 0.952 MPa: elongation at break of 24.7 g/cm3: bending modulus: 17 MPa hardness: VEKA softening point: 44 degrees of brittleness temperature: -85
Manufacturer: Celanese Co
EVA (ethylene vinyl acetate copolymer #) /205W/ DuPont dow
Purpose: hot melt
Features note: amide additive thermal stabilizer: BHT antioxidant
Important beters: melt flow rate: 800 g/10min density: 0.951 g/cm3 filler content: 28%
Manufacturer: Dow DuPont Co