| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) /1044/ Mubolaikesi snow
Purpose: thin film
Features: VAC content of 3.5%, stable air cushion film.
Important beters: melt flow rate: 0.5 g/10min density: 0.929 g/cm3
Manufacturer: United States snow Mubolaikesi company
EVA (ethylene vinyl acetate copolymer #) /V4610H/ Yangzi BASF
Application: foaming
Important beters: melt flow rate: 1.95 g/10min VEKA softening point: filler content of 62 degrees C: 18%
Manufacturer: Yangzi Petrochemical BASF Co., Ltd.
EVA (ethylene vinyl acetate copolymer #) /V3510K/ Yangzi BASF
Usage: other
Important beters: melt flow rate: 4 g/10min tensile strength: elongation at break of 10 MPa: VEKA softening point of: the content of filler at 65 DEG C
Manufacturer: Yangzi Petrochemical BASF Co., Ltd.
EVA (ethylene vinyl acetate copolymer #) /E182L/ Han Hua Total
Uses: coating
Important beters: melt flow rate: 15 g/10min tensile strength: 9.8 MPa elongation at break: 600% bending modulus: MPa hardness: 15 VEKA softening point: 51 degrees of heat debation temperature: 85 degrees of brittleness temperature: -70 C
Manufacturer: Han Hua Total Ltd.
EVA (ethylene vinyl acetate copolymer # Lotte chemical /VS430/)
Application: foaming
Features: process, mechanical properties, particle foam characteristics
Important beters: melt flow rate: 2.5 g/10min density: tensile strength of 0.939 MPa: elongation at break of 13 g/cm3: hardness of 670%: VEKA softening point: 64
Manufacturer: South Korea Lotte Chemical Co Ltd
EVA (ethylene vinyl acetate copolymer # Lotte chemical /VS440/)
Application: foaming
Features: process, mechanical properties, particle foam characteristics
Important beters: melt flow rate: 2.2 g/10min density: tensile strength of 0.935 MPa: elongation at break of 13 g/cm3: hardness of 700%: VEKA softening point: 62
Manufacturer: South Korea Lotte Chemical Co Ltd
EVA (ethylene vinyl acetate copolymer #) /11207/ America flintcomb ash
Purpose: thin film
Features: excellent toughness, low temperature, good heat resistance
Important beters: melt flow rate: 4 g/10min density: tensile strength of 0.931 MPa: elongation at break of 16 g/cm3: hardness of 750%: VEKA softening point: 70
Manufacturer: American flint Hill resources
EVA (ethylene vinyl acetate copolymer # /UE624000/ Leander Basil)
Usage: other
Important beters: melt flow rate: 2.1 g/10min tensile strength: 30.3 MPa elongation at break: 560% hardness: 91 VEKA softening point: 65 degrees of brittleness temperature
Manufacturer: Leander Basel Industrial Company
EVA (ethylene vinyl acetate copolymer #) /ML 20/ of Italy
Usage: other
Features: good resistance to chemicals
Important beters: melt flow rate: 2.5 g/10min tensile strength: 7 MPa bending modulus: 100 MPa hardness: VEKA softening point: 78 degrees of brittleness temperature: -80 C
Manufacturer: Italy Eni
EVA (ethylene vinyl acetate copolymer #) /ML 40/ of Italy
Usage: other
Features: good elasticity and flexibility
Important beters: melt flow rate: 2.5 g/10min tensile strength: 6 MPa bending modulus: 60 MPa hardness: VEKA softening point: 63 degrees of brittleness temperature: -80 C
Manufacturer: Italy Eni