| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) /1834/ Korea China
Usage: other
Features: high elasticity, copolymer, smoothness, oxidation resistance, good processability
Important beters: melt flow rate: 18 g/10min density: 0.96 g/cm3 elongation at break: 1000% hardness: 65 brittleness temperature: -76 C
Manufacturer: South Korea Han Hua integrated chemical company
EVA (ethylene vinyl acetate copolymer #) /EF522/ West Lake
Usage: other
Features: good clarity, low temperature heat sealing and foam applications
Important beters: melt flow rate: 2.5 g/10min density: tensile strength of 0.933 g/cm3: elongation at break of 22 MPa: VEKA softening point: 70
West Lake Chemical Co., Ltd.
EVA (ethylene vinyl acetate copolymer #) /V28280/ Taiwan poly
Usage: other
Low temperature, high transparency
Important beters: melt flow rate: 28 g/10min density: tensile strength of 0.951 MPa: elongation at break of 11.76 g/cm3: hardness of 800%: VEKA softening point: 40 degrees of brittleness temperature: -70 C
Manufacturer: Asia polymerization Limited by Share Ltd
EVA (ethylene vinyl acetate copolymer #) /HERI 07/ Fainplast in Italy
Usage: other
Remarks: foaming properties can be cross-bed
Important beters: density: 0.18 g/cm3 molding shrinkage: tensile strength: 2.6 MPa elongation at break: 330% hardness: 57
Manufacturer: Italy Fainplast company
EVA (ethylene vinyl acetate copolymer #) /WPP551E27/ Southern
Usage: other
Important beters: melt flow rate: 6.5 g/10min density: 0.924 g/cm3 elongation at break: 800% bending modulus: MPa hardness: 19
Manufacturer: American Southern Polymer company
EVA (ethylene vinyl acetate copolymer #) Exxon chemical /UL00220CC3/
Purpose: thin film
Remark: VAC content 20%
Important beters: melt flow rate: 1.8 g/10min density: 0.942 g/cm3
Manufacturer: Exxon Chemicai Company
EVA (ethylene vinyl acetate copolymer #) /E032A/ Han Hua Total
Purpose: thin film
Features: features: transparency, good processing
Important beters: melt flow rate: 0.5 g/10min filler content: 3.5%
Manufacturer: Han Hua Total Ltd.
EVA (ethylene vinyl acetate copolymer # /V215/ Ube)
Application: foaming
Features: VA 15%
Important beters: melt flow rate: 2 g/10min density: tensile strength of 0.93 MPa: elongation at break of 21 g/cm3: 740% bending strength: 60 MPa hardness: VEKA softening point: 68
Manufacturer: Japan Ube
EVA (ethylene vinyl acetate copolymer #) /7920M/ Taiwan plastic
Usage: other
Features: features: good workability, high toughness, good elasticity.
Important beters: melt flow rate: 80 g/10min density: tensile strength of 0.93 MPa: elongation at break of 7 g/cm3: bending modulus: 29 MPa hardness: VEKA softening point: 70 degrees of brittleness temperature: -70 DEG C filler content: 8%
Manufacturer: Taiwan plastics industry Limited by Share Ltd
EVA (ethylene vinyl acetate copolymer #) /V4110D/ Yangzi BASF
Usage: other
Important beters: melt flow rate: 0.275 g/10min tensile strength: elongation at break of 20 MPa: VEKA softening point of: the content of filler at 73 DEG C
Manufacturer: Yangzi Petrochemical BASF Co., Ltd.