| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) /MH 40/ of Italy
Usage: other
Features: high elasticity and good mechanical properties
Important beters: melt flow rate: 1.8 g/10min tensile strength: 5.6 MPa bending modulus: 40 MPa hardness: VEKA softening point: 62 degrees of brittleness temperature: -80 C
Manufacturer: Italy Eni
EVA (ethylene vinyl acetate copolymer #) /HN 70/ of Italy
Purpose: hot melt
Remark: medium flow and high viscosity
Important beters: melt flow rate: 6 g/10min tensile strength: 2.7 MPa elongation at break: 400% bending modulus: MPa hardness: 31 VEKA softening point: 45 degrees of brittleness temperature: -80 C
Manufacturer: Italy Eni
EVA (ethylene vinyl acetate copolymer #) /3173SHB/ DuPont dow
Purpose: thin film
Note: the characteristics of smooth opening agent agent, heat stabilizer, antioxidant BHT
Important beters: melt flow rate: 2.5 g/10min density: VEKA g/cm3 softening point: 65 filler content: 18%
Manufacturer: Dow DuPont Co
EVA (ethylene vinyl acetate copolymer #) /E053/ Han Hua Total
Purpose: thin film
Features: good transparency, workability and tensile strength
Important beters: melt flow rate: 3 g/10min density: 0.928 g/cm3
Manufacturer: Han Hua Total Ltd.
EVA (ethylene vinyl acetate copolymer #) /LD 768.MJ Molding/ Mobil Exxon
Usage: other
Important beters: melt flow rate: 2.3 g/10min tensile strength: 9.45 MPa elongation at break: 800% bending modulus: MPa hardness of 31: VEKA softening point: 49
Manufacturer: Exxon Mobil Corp
EVA (ethylene vinyl acetate copolymer #) /48/9900 CP/80/ Italy problem
Usage: other
Thermal conductivity
Important beters: density: 2.66 g/cm3 molding shrinkage rate: 0.55% VEKA softening point: thermal debation temperature of 35 degrees C: 50 C
Manufacturer: Italy branch company
EVA (ethylene vinyl acetate copolymer #) /HLP 200/ API in Italy
Usage: other
Remark: gloss, good flexibility in cross-bing
Important beters: density: 0.2 g/cm3 tensile strength: 2 MPa elongation: 220% hardness: 37
Manufacturer: Italy API company
EVA (ethylene vinyl acetate copolymer #) /NUC-3765D/ Japan Younika
Usage: other
Features note: Slip level:N
Important beters: melt flow rate: 0.9 g/10min density: 0.94 g/cm3 tensile strength: 28 MPa elongation: 750%
Manufacturer: Japan Younika Co.
EVA (ethylene vinyl acetate copolymer #) Exxon chemical /UL00119CC3/
Purpose: thin film
Remark: VAC content 19%
Important beters: melt flow rate: 0.65 g/10min density: 0.941 g/cm3
Manufacturer: Exxon Chemicai Company
EVA (ethylene vinyl acetate copolymer #) Exxon chemical /UL00218CC3/
Usage: other
Note: the characteristics of the content of VAC is 18%, the film
Important beters: melt flow rate: 1.7 g/10min density: 0.939 g/cm3
Manufacturer: Exxon Chemicai Company