| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) /PA-420/ Repsol of Spain
Usage: other
Features: good flexibility. Good compatibility with wax, asphalt and filler
Important beters: melt flow rate: 20 g/10min density: tensile strength of 0.94 MPa: elongation at break of 11 g/cm3: hardness of 780%: VEKA softening point: 53
Manufacturer: YPF of Spain
EVA (ethylene vinyl acetate copolymer #) /UE-1203/ Brazil Quattor
Purpose: thin film
Features: good machining perbance and compatibility, good mechanical strength and high stress cracking at low temperature
Important beters: melt flow rate: 0.32 g/10min density: tensile strength of 0.933 MPa: elongation at break of 17 g/cm3: hardness of 770%: VEKA softening point: 76
Manufacturer: Brazil Quattor Petrochemical Industries Co
EVA (ethylene vinyl acetate copolymer #) /FD23/ Italy
Purpose: thin film
Features: good optical properties, high impact resistance, tensile strength, elongation at break, low creep
Important beters: melt flow rate: 0.5 g/10min tensile strength: 26 MPa elongation at break: 600% hardness: 44 VEKA softening point: 85 degrees of brittleness temperature
Manufacturer: Italy Eni
EVA (ethylene vinyl acetate copolymer #) /CA-2220G/ Repsol of Spain
Purpose: thin film
UV absorbers and antioxidants
Important beters: melt flow rate: 0.28 g/10min density: 0.935 g/cm3 tensile strength: 21 MPa elongation: 700%
Manufacturer: YPF of Spain
EVA (ethylene vinyl acetate copolymer #) /CA-2720G/ Repsol of Spain
Purpose: thin film
UV absorbers and antioxidants
Important beters: melt flow rate: 0.25 g/10min density: 0.949 g/cm3 tensile strength: 23 MPa elongation: 750%
Manufacturer: YPF of Spain
EVA (ethylene vinyl acetate copolymer #) /CA-2721G/ Repsol of Spain
Purpose: thin film
UV absorbers and antioxidants
Important beters: melt flow rate: 0.45 g/10min density: 0.953 g/cm3 tensile strength: 26 MPa elongation: 750%
Manufacturer: YPF of Spain
EVA (ethylene vinyl acetate copolymer #) /CM22-1/ Ishida
Usage: other
Features: good stress cracking resistance, workability, transparency and good surface gloss
Important beters: melt flow rate: 25 g/10min density: tensile strength of 0.924 MPa: elongation at break of 12 g/cm3: hardness of 650%: VEKA softening point: 73 degrees of brittleness temperature: -70 DEG C filler content: 7%
Manufacturer: Showa Electric Corporation
EVA (ethylene vinyl acetate copolymer #) /7350M/ Taiwan chemical fiber
Usage: other
Features: high elasticity, copolymer, crossbing, good flexibility, good chemical resistance
Important beters: melt flow rate: 2.5 g/10min density: tensile strength of 0.938 MPa: elongation at break of 14.7 g/cm3: bending modulus: 14.7 MPa hardness: VEKA softening point: 60 degrees of brittleness temperature: -70
Manufacturer: Taiwan chemical fiber Limited by Share Ltd
EVA (ethylene vinyl acetate copolymer #) /7660M/ Taiwan chemical fiber
Usage: other
Features: copolymer, optical properties, processability, good, crossbable, good thermal sealing, good toughness
Important beters: melt flow rate: 20 g/10min density: tensile strength of 0.94 MPa: elongation at break of 10.8 g/cm3: bending modulus: 12.7 MPa hardness: 32 hot debation temperature: 60 degrees of brittleness temperature: -70 C
Manufacturer: Taiwan chemical fiber Limited by Share Ltd
EVA (ethylene vinyl acetate copolymer #) /PA-536/ Repsol of Spain
Usage: Profiles
Features: oxidation resistance, good processability, compliance with food contact
Important beters: melt flow rate: 0.7 g/10min density: elongation at break of 0.941 g/cm3: VEKA softening point: 62
Manufacturer: YPF of Spain