| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) /1811/ America Serra nice
Usage: other
Important beters: melt flow rate: 1.6 g/10min density: tensile strength of 0.937 MPa: elongation at break of 20 g/cm3: hardness of 740%: VEKA softening point: 64 degrees of brittleness temperature: -85 C
Manufacturer: Celanese Co
EVA (ethylene vinyl acetate copolymer #) /1850A/ America Serra nice
Usage: other
Important beters: melt flow rate: 150 g/10min density: tensile strength of 0.935 MPa: elongation at break of 7 g/cm3: bending modulus: 42 MPa hardness: VEKA softening point: 49 degrees of brittleness temperature: -40
Manufacturer: Celanese Co
EVA (ethylene vinyl acetate copolymer #) /2803G/ America Serra nice
Usage: other
Important beters: melt flow rate: 3 g/10min density: tensile strength of 0.952 MPa: elongation at break of 24 g/cm3: bending modulus: 21 MPa hardness: VEKA softening point: 44 degrees of brittleness temperature: -85
Manufacturer: Celanese Co
EVA (ethylene vinyl acetate copolymer #) /2842AC/ America Serra nice
Usage: other
Important beters: density: 0.941 g/cm3 tensile strength: 2.5 MPa elongation at break: 600% bending modulus: MPa hardness: 14
Manufacturer: Celanese Co
EVA (ethylene vinyl acetate copolymer #) / 605A/ America Serra nice
Usage: other
Important beters: melt flow rate: 0.15 g/10min density: tensile strength of 0.923 g/cm3: elongation at break of 20 MPa: bending modulus: 245 MPa hardness: 51
Manufacturer: Celanese Co