| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
LLDPE (linear low density polyethylene # linear polyethylene) /DMDA145/ Guangzhou petrochemical
Usage: other
Important beters: melt flow rate: 12 g/10min density: 0.926 g/cm3
Manufacturer: China Petroleum Chemical Co Guangzhou branch
LLDPE (linear low density polyethylene # linear polyethylene) /DMDA8320/ Guangzhou petrochemical
Usage: other
Important beters: melt flow rate: 20 g/10min density: 0.924 g/cm3
Manufacturer: China Petroleum Chemical Co Guangzhou branch
LLDPE (linear low density polyethylene # linear polyethylene) /DMDA7144/ Guangzhou petrochemical
Usage: other
Important beters: melt flow rate: 20 g/10min density: 0.924 g/cm3
Manufacturer: China Petroleum Chemical Co Guangzhou branch
LLDPE (linear low density polyethylene # linear polyethylene) /DA2201/ Japan Sea
Usage: other
Important beters: melt flow rate: 0.8 g/10min density: tensile strength of 0.93 g/cm3: elongation at break of 33 MPa: bending modulus: 500 MPa hardness: 63
Manufacturer: Japan Offshore Oil Resources Development Corporation
LLDPE (linear low density polyethylene # linear polyethylene) /DA4600/ Japan Sea
Usage: other
Important beters: melt flow rate: 6.4 g/10min density: tensile strength of 0.91 g/cm3: elongation at break of 13 MPa: bending modulus: 200 MPa hardness: 53
Manufacturer: Japan Offshore Oil Resources Development Corporation
LLDPE (linear low density polyethylene # linear polyethylene) /L6090/ Japan Sea
Usage: other
Important beters: melt flow rate: 1.2 g/10min density: tensile strength of 0.93 g/cm3: elongation at break of 22 MPa: bending modulus: 390 MPa hardness: 60
Manufacturer: Japan Offshore Oil Resources Development Corporation
LLDPE (linear low density polyethylene # linear polyethylene) /HM-265/ RAVAGO of Belgium
Usage: other
Remarks: machinability, good
Important beters: melt flow rate: 1 g/10min
Manufacturer: Belgium RAVAGO group
LLDPE (linear low density polyethylene # type high pressure polyethylene) /UF240/ Japan JPC
Purpose: thin film
General purpose
Important beters: melt flow rate: 2.1 g/10min density: notched impact strength of g/cm3: 230 bending modulus: 200 MPa hardness: VEKA softening point of 49: 102 degrees of brittleness temperature: -70 C
Manufacturer: Japan JPC company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /UF340/ Japan JPC
Purpose: thin film
General purpose
Important beters: melt flow rate: 1.9 g/10min density: notched impact strength of g/cm3: 190 bending modulus: 210 MPa hardness: VEKA softening point of 51: 102 degrees of brittleness temperature: -70 C
Manufacturer: Japan JPC company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /UF840/ Japan JPC
Purpose: thin film
Remark: rigidity, high
Important beters: melt flow rate: 1.5 g/10min density: notched impact strength of g/cm3: 160 bending modulus: 370 MPa hardness: VEKA softening point of 55: 114 degrees of brittleness temperature: -70 C
Manufacturer: Japan JPC company