产品详情
长期供应德国拜耳 PC ET3117 价格合理,诚信经营，可全国供货（广东省内 免费送货上门）。
“十年老店，完备售后，信誉信赖” 是专业塑胶原料供应商
本司货源稳定充足，发货准时，交期和质量均有保障！
根据客户要求，可提供塑胶原料相关报告。如：ROHS(SGS)报告，UL认证，材质证明及物质安全资料表（MSDS）！
欢迎来电咨询7*24全天候服务热线：13686017791 易小姐 QQ：335171600
介绍————————
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
LLDPE (linear low density polyethylene # type high-pressure polyethylene) /D201/ Australia Qenos
Usage: other
Features: antioxidant
Important beters: melt flow rate: 0.45 g/10min density: 0.922 g/cm3 tensile strength: 10 MPa elongation: 480%
Manufacturer: Australian Qenos company
LLDPE (linear low density polyethylene # type high-pressure polyethylene) /XLF197/ Australia Qenos
Usage: other
Features: high definition
Important beters: melt flow rate: 5.5 g/10min density: 0.92 g/cm3 tensile strength: 9 MPa elongation: 120%
Manufacturer: Australian Qenos company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LBH 0117/ Braskem in Brazil
Usage: other
Features: copolymer, good processing, monomer, low density
Important beters: melt flow rate: 0.75 g/10min density: 0.918 g/cm3 tensile strength: 12 MPa elongation: 820%
Manufacturer: Brazil chemical company
LLDPE (linear low density polyethylene # linear polyethylene) /2511F/ Japan Primeman
Usage: other
Features: good processing, high slip
Important beters: melt flow rate: 1.3 g/10min density: bending modulus of 0.924 g/cm3: 250 MPa hardness: VEKA softening point: 105
Manufacturer: Japan Puri polymer Co.
LLDPE (linear low density polyethylene # linear polyethylene) /2074F/ Japan Primeman
Usage: other
Remark: good flow, good rigidity
Important beters: melt flow rate: 25 g/10min density: bending modulus of 0.94 g/cm3: 570 MPa hardness: VEKA softening point: 117
Manufacturer: Japan Puri polymer Co.
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LB 0117/ Braskem in Brazil
Usage: other
Features: butene monomer, copolymer, good processing, low density
Important beters: melt flow rate: 0.75 g/10min density: 0.918 g/cm3 tensile strength: 12 MPa elongation: 840%
Manufacturer: Brazil chemical company
LLDPE (linear low density polyethylene # linear polyethylene) /CM50/ Italy
Usage: other
Features: antioxidants, high stiffness
Important beters: melt flow rate: 4.1 g/10min density: elongation at break of 0.938 g/cm3: VEKA softening point: 118 degrees of brittleness temperature: -70
Manufacturer: Italy Eni
LLDPE (linear low density polyethylene # linear polyethylene) /0234H/ Japan Primeman
Usage: other
Features: good machining perbance, high slip
Important beters: melt flow rate: 2 g/10min density: bending modulus of 0.921 g/cm3: 200 MPa hardness: VEKA softening point: 102
Manufacturer: Japan Puri polymer Co.
LLDPE (linear low density polyethylene # linear polyethylene) /0144H/ Japan Primeman
Usage: other
Features: good machining perbance, high slip
Important beters: melt flow rate: 1.2 g/10min density: 0.924 g/cm3 hardness: VEKA softening point: 103
Manufacturer: Japan Puri polymer Co.
LLDPE (linear low density polyethylene # linear polyethylene) /0134H/ Japan Primeman
Usage: other
Features: good machining perbance, high slip
Important beters: melt flow rate: 1.2 g/10min density: 0.921 g/cm3 hardness: VEKA softening point: 101
Manufacturer: Japan Puri polymer Co.