| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
LLDPE (linear low density polyethylene # type high pressure polyethylene) /PF-0218-B/ Canada NOVA
Usage: other
Characteristic remarks:
Important beters: melt flow rate: 2 g/10min density: 0.918 g/cm3 tensile strength: 10 MPa elongation: 760%
Manufacturer: NOVA chemical company of Canada
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LL104AA/ M.Holland
Usage: other
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3 tensile strength: 33.1 MPa elongation: 600%
Manufacturer: American M.Holland company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LL104AM/ M.Holland
Usage: other
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3 tensile strength: 33.1 MPa elongation: 600%
Manufacturer: American M.Holland company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LL104MM/ M.Holland
Usage: other
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3 tensile strength: 33.1 MPa elongation: 600%
Manufacturer: American M.Holland company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /PE-533/ MDI
Usage: other
Features: dispersible tablets, good UV resistance, low density, lubrication
Important beters: melt flow rate: 4 g/10min density: 1.11 g/cm3
Manufacturer: American MDI company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /PE-540/ MDI
Usage: other
Features: dispersible tablets, good UV resistance, low density, lubrication
Important beters: melt flow rate: 20 g/10min density: 1.15 g/cm3
Manufacturer: American MDI company
LLDPE (linear low density polyethylene # linear polyethylene) /HM-267/ Milstein
Usage: other
Features: good processability, good color and transparency
Important beters: melt flow rate: 9 g/10min
Manufacturer: Milstein (Muehlstein)
LLDPE (linear low density polyethylene # type high pressure polyethylene) /DFDC-7050/ Fujian United
Purpose: thin film
Catalyst: UCAT-J copolymerization monomer: butene -1
Important beters: melt flow rate: 2 g/10min density: 0.918 g/cm3
Manufacturer: Fujian United Petrochemical Co., Ltd.
LLDPE (linear low density polyethylene # type high pressure polyethylene) /DFDA-7047/ Fujian United
Purpose: thin film
Catalyst: UCAT-J copolymerization monomer: butene -1
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3
Manufacturer: Fujian United Petrochemical Co., Ltd.
LLDPE (linear low density polyethylene # type high pressure polyethylene) /DFDC-7080/ Fujian United
Purpose: thin film
Catalyst: UCAT-J copolymerization monomer: butene -1
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3
Manufacturer: Fujian United Petrochemical Co., Ltd.