| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
LLDPE (linear low density polyethylene # linear polyethylene) /AC481R/ Japan Sea
Usage: other
Low density
Important beters: melt flow rate: 2.2 g/10min density: tensile strength of 0.939 MPa: elongation at break of 16 g/cm3: hardness of 720%: VEKA softening point: 112 degrees of brittleness temperature: -70 C
Manufacturer: Japan Offshore Oil Resources Development Corporation
LLDPE (linear low density polyethylene # type high pressure polyethylene) /UR951/ Japan JPC
Usage: other
Features: rigid, high, high ESCR (stress resistant crack)
Important beters: melt flow rate: 3.5 g/10min density: bending modulus of 0.938 g/cm3: 490 MPa hardness: VEKA softening point: 116 degrees of brittleness temperature: -70
Manufacturer: Japan JPC company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /14X01/ Iran JPC
Purpose: thin film
Features: high rigidity
Important beters: melt flow rate: 0.95 g/10min density: 0.914 g/cm3 tensile strength: 40 MPa elongation: 890%
Manufacturer: Iran JPC company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /14ZF8/ Iran JPC
Purpose: thin film
Features: good processability
Important beters: melt flow rate: 0.75 g/10min density: 0.914 g/cm3 tensile strength: 28 MPa elongation: 680%
Manufacturer: Iran JPC company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /09-046 F/ DexPlastomer in Holland
Purpose: thin film
Features: toughness, puncture resistance, sealing perbance, optical properties, self adhesion
Important beters: melt flow rate: 4.4 g/10min density: VEKA g/cm3 softening point: 89
Manufacturer: Holland DexPlastomer company
LLDPE (linear low density polyethylene # linear polyethylene) /HS-7065 NT 7/ dow
Purpose: thin film
Features: good toughness and stiffness
Important beters: melt flow rate: 0.8 g/10min density: tensile strength of 0.9289 g/cm3: elongation at break of 54 MPa: VEKA softening point: 116
Manufacturer: Dow Chemical Corporation
LLDPE (linear low density polyethylene # linear polyethylene) /2267A/ dow
Usage: other
Remark: toughness 21 CFR C (a) 3.1
Important beters: melt flow rate: 0.85 g/10min density: tensile strength of 0.917 g/cm3: VEKA softening point of 42 MPa
Manufacturer: Dow Chemical Corporation
LLDPE (linear low density polyethylene # type high pressure polyethylene) /1810 H/ Total of France
Purpose: thin film
Properties: butene comonomer, smoothness, oxidation resistance
Important beters: melt flow rate: 1 g/10min density: VEKA g/cm3 softening point: 100
Manufacturer: Total Petrochemical Industries Co
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LL1091/ M.Holland
Usage: other
Features: good heat sealing, good toughness
Important beters: melt flow rate: 1 g/10min density: 0.918 g/cm3 tensile strength: 20 MPa elongation: 600%
Manufacturer: American M.Holland company
LLDPE (linear low density polyethylene # type high pressure polyethylene) /LL2406AA/ Sidpec in Egypt
Use: pipe
Important beters: melt flow rate: 0.65 g/10min density: tensile strength of 0.924 g/cm3: 11.8 MPa elongation at break: 1000% bending modulus: 400 MPa
Manufacturer: Egypt Sidi Krier Petrochemical Industries Co