| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
EVA (ethylene vinyl acetate copolymer #) Exxon chemical /UL15028/
Usage: other
Important beters: melt flow rate: 150 g/10min density: tensile strength of 0.947 g/cm3: elongation at break of 3.4 MPa: hardness: 72
Manufacturer: Exxon Chemicai Company
EVA (ethylene vinyl acetate copolymer #) Exxon chemical /UL00226/
Usage: other
Remark: VAC content 26%
Important beters: melt flow rate: 2 g/10min density: 0.95 g/cm3
Manufacturer: Exxon Chemicai Company
EVA (ethylene vinyl acetate copolymer #) /V2624GX/ Germany BASF
Purpose: thin film
Important beters: melt flow rate: 1 g/10min density: 0.925 g/cm3
Manufacturer: Basf Inc
EVA (ethylene vinyl acetate copolymer #) /E156W/ Han Hua Total
Usage: other
Important beters: melt flow rate: 6 g/10min filler content: 15%
Manufacturer: Han Hua Total Ltd.
EVA (ethylene vinyl acetate copolymer # /VS440/ Hyundai)
Usage: other
Important beters: melt flow rate: 1.5 g/10min density: hardness of 0.935 g/cm3: VEKA softening point: 66 degrees of brittleness temperature: -70 DEG C filler content: 15%
Manufacturer: Korea Hyundai Petrochemical Company