| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
PC/ABS (PC and ABS alloy) /CS9703/ Nanjing Li Han
Usage: other
Features: features: PC/ABS alloy flame retardant
Important beters: melt flow rate: 22 g/10min density: 1.2 g/cm3 impact strength: 4500 tensile strength: 56 MPa elongation: 100% bending strength: 98 MPa flexural modulus: 2500 MPa hardness: 110 thermal debation temperature: 110 degrees
Manufacturer: Nanjing Li Han Chemical Co., Ltd.
PC/ABS (PC and ABS alloy) /5644/ Shenzhen Zhicheng
Usage: other
Characteristic feature: heat resistance of PC/ABS alloy is PC, dimensional stability and good mechanical properties, compared with PC, but also has low melt viscosity, good processability and low price; and also can reduce the internal stress and the impact strength of products on the sensitivity of the thickness of the products, therefore, is PC/ABS alloy on the basis of the above effects of PC/ABS alloy. The flame retardancy is extended to the application field.
Important beters: density: 1.13 g/cm3 molding shrinkage rate: 0.6% notched impact strength: tensile strength: 70 MPa elongation at break: 134% bending strength: 109 MPa bending modulus: 2870 MPa thermal debation temperature: 115 C
Manufacturer: Shenzhen Zhicheng plastic materials factory
ABS/PC (ABS and PC alloy #) /PC / ABS 720 BK/ TPC
Usage: other
Important beters: melt flow rate: 1.5 g/10min density: water absorption rate of 1.21 g/cm3: 0.1% tensile strength: MPa bending strength: 98.6 MPa bending modulus: 2620 MPa hardness: 115 hot debation temperature: 135 C
Manufacturer: American TP Composites company
ABS/PC (ABS and PC alloy #) /PC / ABS 88 GF10/ TPC
Usage: other
Important beters: density: 1.2 g/cm3 water absorption: 0.1% molding shrinkage rate: 0.4% tensile strength: MPa bending strength: 103 MPa bending modulus: 4070 MPa hardness: 119 hot debation temperature: 116 C
Manufacturer: American TP Composites company
ABS/PC (ABS and PC alloy #) /120/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division
ABS/PC (ABS and PC alloy #) /130/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division
ABS/PC (ABS and PC alloy #) /150/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division
ABS/PC (ABS and PC alloy #) /170/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division
ABS/PC (ABS and PC alloy #) /190/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division
ABS/PC (ABS and PC alloy #) /210/ Korea Miyaki
Usage: other
Important beters:
Manufacturer: SAMYANG engineering plastics division