| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
ABS/PC (ABS and PC alloy # / 2583C HEC/ RTP)
Usage: other
Important beters: density: 1.29 g/cm3 water absorption: 0.1% molding shrinkage rate: 0.15% tensile strength: MPa bending strength: 152 MPa bending modulus: 9650 MPa thermal debation temperature: 121 C
Manufacturer: American RTP company
ABS/PC (ABS PC /2599 X C/ alloy #) 113384 RTP
Usage: other
Important beters: density: 1.34 g/cm3 molding shrinkage rate: 0.6% tensile strength: MPa bending strength: 85 MPa bending modulus: 2410 MPa
Manufacturer: American RTP company
ABS/PC (ABS PC /2599 X 96121/ alloy #) RTP
Usage: other
Important beters: melt flow rate: 17 g/10min density: 1.12 g/cm3 molding shrinkage rate: 0.6% tensile strength: MPa bending strength: 93.1 MPa bending modulus: 2760 MPa thermal debation temperature: 107 C
Manufacturer: American RTP company
ABS/PC (ABS and PC alloy #) /HE-1071/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 47 g/10min density: 1.2 g/cm3 molding shrinkage rate: 0.3% tensile strength: 64 MPa flexural strength: 93 MPa flexural modulus: 3040 MPa hardness: 114 VEKA softening point of 142 DEG C heat debation temperature: 130 degrees
Manufacturer: Korea first wool weaving Co.
ABS/PC (ABS PC and /C130/ perrite alloy #)
Usage: other
Features: granular material
Important beters: melt flow rate: 20 g/10min density: 1.15 g/cm3 impact strength: 45 tensile strength: 55 MPa elongation: 50% bending strength: 80 MPa flexural modulus: 2300 MPa VEKA softening point: debation temperature of 130 DEG C heat: 110 degrees
Manufacturer: perrite, UK
ABS/PC (ABS PC and /NC-8810M/ alloy # America Nova)
Usage: other
Important beters: melt flow rate: 12 g/10min density: notched impact strength of g/cm3: 534 tensile strength: 52.4 MPa bending strength: 75.8 MPa bending modulus: 2070 MPa
Manufacturer: Nova Polymer Co
PC/ABS (PC and ABS alloy) /T-3300-5002/ Shanghai complex
Usage: other
Important beters: density: 1.2 g/cm3 notched impact strength: tensile strength: 56 MPa elongation at break: 17% bending strength: 134 MPa hardness: 110 hot debation temperature: 115 C
Manufacturer: Shanghai Industrial Development Co., Ltd.
PC/ABS (PC and ABS alloy) /T-3300-5004/ Shanghai complex
Usage: other
Important beters: density: 1.2 g/cm3 notched impact strength: tensile strength: 55 MPa elongation at break: 20% bending strength: 115 MPa hardness: 110 hot debation temperature: 115 C
Manufacturer: Shanghai Industrial Development Co., Ltd.
PC/ABS (PC and ABS alloy) /7350/ Jubilee (Trinseo)
Usage: other
Important beters: melt flow rate: 25 g/10min density: 1.18 g/cm3 molding shrinkage rate: 0.4% notched impact strength: 700 tensile strength: 53 MPa elongation: 130% bending strength: 87 MPa flexural modulus of 2600 MPa hot debation temperature: 105 degrees
Manufacturer: Sheng Xi Ao (Trinseo) Company
PC/ABS (PC and ABS alloy) /7502/ Jubilee (Trinseo)
Usage: other
Glass fiber reinforced 20%.
Important beters: melt flow rate: 17 g/10min molding shrinkage rate: 0.15% notched impact strength: 110 bending modulus: 6200 MPa thermal debation temperature: 120 C
Manufacturer: Sheng Xi Ao (Trinseo) Company