| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Linear Mold Shrinkage, Flow |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Index of Compound |
23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 |
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |
其他型号参数与生产商——————————
ABS/PC (ABS PC and /GN-5001EF/LG chemical # alloy)
Usage: other
Important beters: melt flow rate: 2.2 g/10min density: tensile strength of 1.8 g/cm3: MPa bending strength: 103 MPa bending modulus: 2420 MPa thermal debation temperature: 108 C
Manufacturer: Korea LG chemical company
ABS/PC (ABS PC and /GP-5008A/LG chemical # alloy)
Usage: other
Important beters: melt flow rate: 18 g/10min density: water absorption rate of 1.06 g/cm3: VEKA softening point of 0.16%: thermal debation temperature of 97.7 degrees C: C
Manufacturer: Korea LG chemical company
ABS/PC (ABS PC and /HP-5008/LG chemical # alloy)
Usage: other
Important beters: melt flow rate: 6.3 g/10min density: g/cm3 molding shrinkage: 0.5% notched impact strength: 392 tensile strength: MPa bending strength: 87.8 MPa bending modulus: 2220 MPa thermal debation temperature: 106
Manufacturer: Korea LG chemical company
ABS/PC (ABS PC /2500 A HB/ alloy #) RTP
Usage: other
Important beters: density: 1.15 g/cm3 molding shrinkage rate: 0.5% tensile strength: MPa bending strength: 96.5 MPa bending modulus: 2760 MPa thermal debation temperature: 110 C
Manufacturer: American RTP company
ABS/PC (ABS PC /2500 HF A/ alloy #) RTP
Usage: other
Important beters: density: 1.15 g/cm3 molding shrinkage rate: 0.6% tensile strength: MPa bending strength: 89.6 MPa bending modulus: 2760 MPa thermal debation temperature: 110 C
Manufacturer: American RTP company
ABS/PC (ABS PC /2500 UV/ RTP alloy #)
Usage: other
Important beters: density: 1.14 g/cm3 water absorption: 0.15% molding shrinkage rate: 0.6% tensile strength: MPa bending strength: 82.7 MPa bending modulus: 2340 MPa hardness: 116 hot debation temperature: 110 C
Manufacturer: American RTP company
ABS/PC (ABS PC /2560.75 FR/ RTP alloy #)
Usage: other
Important beters: density: 1.31 g/cm3 water absorption: 0.12% molding shrinkage rate: 0.5% tensile strength: MPa bending strength: 103 MPa bending modulus: 2620 MPa
Manufacturer: American RTP company
ABS/PC (ABS PC /2583 HEC FR/ alloy #) RTP
Usage: other
Important beters: density: 1.42 g/cm3 water absorption: 0.1% molding shrinkage rate: 0.05% tensile strength: MPa bending strength: 165 MPa bending modulus: 10300 MPa
Manufacturer: American RTP company
ABS/PC (ABS PC /2599 X B/ alloy #) 87260 RTP
Usage: other
Important beters: density: 1.18 g/cm3 molding shrinkage rate: 0.5% tensile strength: MPa bending strength: 103 MPa bending modulus: 3450 MPa
Manufacturer: American RTP company
ABS/PC (ABS and PC alloy #) /HE-1051/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 7 g/10min density: 1.13 g/cm3 molding shrinkage rate: 0.5% tensile strength: 51 MPa flexural strength: 73 MPa flexural modulus: 7960 MPa hardness: 109 VEKA softening point of 138 DEG C heat debation temperature: 126 degrees
Manufacturer: Korea first wool weaving Co.