产品详情
长期供应科思创(原:拜耳) TPU W DP89051D 价格合理,诚信经营，可全国供货（广东省内 免费送货上门）。
“十年老店，完备售后，信誉信赖” 是专业塑胶原料供应商
本司货源稳定充足，发货准时，交期和质量均有保障！
根据客户要求，可提供塑胶原料相关报告。如：ROHS(SGS)报告，UL认证，材质证明及物质安全资料表（MSDS）！
欢迎来电咨询7*24全天候服务热线：13686017791 易小姐 QQ：335171600
介绍————————
Physical Properties
Metric
English
Comments
Density
1.20 g/cc
0.0434 lb/in3
ISO 1183
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
85
85
ISO 868
Hardness, Shore D
33
33
ISO 868
Tensile Strength
2.00 MPa
@Strain 10.0 %
290 psi
@Strain 10.0 %
200 mm/min; DIN 53504
4.70 MPa
@Strain 50.0 %
682 psi
@Strain 50.0 %
200 mm/min; DIN 53504
5.80 MPa
@Strain 100 %
841 psi
@Strain 100 %
200 mm/min; DIN 53504
16.6 MPa
@Strain 300 %
2410 psi
@Strain 300 %
200 mm/min; DIN 53504
Tensile Strength, Ultimate
52.0 MPa
7540 psi
200 mm/min; DIN 53504
Elongation at Break
531 %
531 %
200 mm/min; DIN 53504
Tensile Modulus
0.0210 GPa
@Temperature 60.0 °C
3.05 ksi
@Temperature 140 °F
storage; ISO 6721-1,-4
其他型号参数与生产商——————————
PC/ABS (PC & ABS) /1210HI/ Shenzhen Asia Pacific
Usage: other
Features: impact resistance
Important beters: melt flow rate: 7 g/10min density: 1.13 g/cm3 molding shrinkage rate: 0.65% notched impact strength: 62 tensile strength: 59 MPa elongation: 160% bending strength: 91 MPa flexural modulus of 2452 MPa hot debation temperature: 108 degrees
Shenzhen Yatai Industrial Co., Ltd.
ABS/PC (ABS and PC alloy #) /HAC-8250FR/ Korea Kumho
Usage: other
Important beters: melt flow rate: 20 g/10min density: g/cm3 molding shrinkage rate: 0.5% tensile strength: 53.9 MPa bending strength: 68.6 MPa bending modulus: 1960 MPa hardness: 110 hot debation temperature: 100 C
Manufacturer: Kumho Korea Petroleum Chemical Corporation
PC/ABS (PC and ABS alloy) /LP40/ Shanghai crystal
Usage: other
Low temperature resistance
Important beters: density: 1.15 g/cm3 absorption rate: 0.3% molding shrinkage rate: 0.5% notched impact strength: 55 tensile strength: 56 MPa elongation: 160% bending strength: 83 MPa flexural modulus of 2100 MPa hot debation temperature: 113 degrees
Manufacturer: Shanghai Crystal Engineering Plastic Technology Co., Ltd.
ABS/PC (ABS PC /2500 TFE FR/ alloy #) 20 RTP
Usage: other
Important beters: density: 1.36 g/cm3 water absorption: 0.1% molding shrinkage rate: 0.6% tensile strength: MPa bending strength: 89.6 MPa bending modulus: 2410 MPa thermal debation temperature: 93.3 C
Manufacturer: American RTP company
ABS/PC (ABS PC /2599X87260C/ RTP alloy #)
Usage: other
Important beters: density: 1.18 g/cm3 water absorption: 0.12% molding shrinkage rate: 0.5% bending strength: MPa bending modulus: 3450 MPa thermal debation temperature: 93.3 C
Manufacturer: American RTP company
ABS/PC (ABS and PC alloy #) /HI-1003BP/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 36 g/10min density: 1.1 g/cm3 absorption rate: 0.2% tensile strength: 53.8 MPa flexural strength: 75.8 MPa flexural modulus: 2140 MPa hardness: 107 VEKA softening point of 112 DEG C heat debation temperature: 102 degrees
Manufacturer: Korea first wool weaving Co.
ABS/PC (ABS and PC / HR-1008BN/ alloy #) Samsung Cheil
Usage: other
Important beters: melt flow rate: 35 g/10min density: 1.13 g/cm3 molding shrinkage rate: 0.5% tensile strength: 49 MPa flexural strength: 68.3 MPa flexural modulus: 1930 MPa hardness: 114 VEKA softening point of 120 DEG C heat debation temperature: 105 degrees
Manufacturer: Korea first wool weaving Co.
ABS/PC (ABS and PC alloy #) /NH-1000TR/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 40 g/10min density: 1.2 g/cm3 absorption rate: 0.2% molding shrinkage rate: 0.5% tensile strength: 60 MPa flexural strength: 80 MPa flexural modulus: 2550 MPa hardness: 117 VEKA softening point of 90 DEG C heat debation temperature: 80 degrees
Manufacturer: Korea first wool weaving Co.
ABS/PC (ABS and PC alloy #) /NH-1000TS/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 55 g/10min density: molding shrinkage rate of 1.18 g/cm3: 0.5% tensile strength: MPa bending strength: 75.8 MPa bending modulus: VEKA softening point of 2480 MPa: thermal debation temperature: 85 C
Manufacturer: Korea first wool weaving Co.
ABS/PC (ABS and PC alloy #) /NH-1017SB/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 32 g/10min density: 1.18 g/cm3 molding shrinkage rate: 0.5% notched impact strength: 510 tensile strength: 59 MPa flexural strength: 91 MPa flexural modulus: 2410 MPa hardness: 119 thermal debation temperature: 99.3 degrees
Manufacturer: Korea first wool weaving Co.