Physical Properties
Metric
English
Comments
Density
1.20 g/cc
0.0434 lb/in3
ISO 1183
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
85
85
ISO 868
Hardness, Shore D
33
33
ISO 868
Tensile Strength
2.00 MPa
@Strain 10.0 %
290 psi
@Strain 10.0 %
200 mm/min; DIN 53504
4.70 MPa
@Strain 50.0 %
682 psi
@Strain 50.0 %
200 mm/min; DIN 53504
5.80 MPa
@Strain 100 %
841 psi
@Strain 100 %
200 mm/min; DIN 53504
16.6 MPa
@Strain 300 %
2410 psi
@Strain 300 %
200 mm/min; DIN 53504
Tensile Strength, Ultimate
52.0 MPa
7540 psi
200 mm/min; DIN 53504
Elongation at Break
531 %
531 %
200 mm/min; DIN 53504
Tensile Modulus
0.0210 GPa
@Temperature 60.0 °C
3.05 ksi
@Temperature 140 °F
storage; ISO 6721-1,-4
其他型号参数与生产商——————————
PC/ABS (PC and ABS alloy) /DY2000/ multi benefit plastics
Usage: other
Important beters: melt flow rate: 7 g/10min density: g/cm3 molding shrinkage: 0.3% notched impact strength: 60 tensile strength: MPa bending strength: 77.42 MPa bending modulus: 2538 MPa thermal debation temperature: 112
Manufacturer: Yuyao Yi Yi Plastic Technology Co., Ltd.
ABS/PC (ABS PC /050/85S-UV/ Almaak alloy #) Germany
Usage: other
Important beters: density: 1.15 g/cm3 water absorption: notch impact strength: 58 VEKA softening point: thermal debation temperature of 1398 degrees: 115 degrees C
Manufacturer: Almaak, Germany
PC/ABS (PC and ABS alloy) /GP-5306F/LG chemistry
Usage: other
Feature note: fill level
Important beters: density: 1.44 g/cm3 notched impact strength: tensile strength: 127.451 MPa elongation at break: 3% bending strength: 186.274 MPa bending modulus: 8333.33 MPa hardness: 82
Manufacturer: Korea LG chemical company
PC/ABS (PC and ABS alloy) /GP-5006AF/LG chemistry
Usage: other
Features: features: anti flammability
Important beters: density: 1.22 g/cm3 notched impact strength: tensile strength: 61.274 MPa elongation at break: 120% bending strength: 96.078 MPa bending modulus: 2411.77 MPa hardness: 120
Manufacturer: Korea LG chemical company
PC/ABS (PC and ABS alloy) /MP-5001AF/LG chemistry
Usage: other
Features note: plating level of fire resistance, electroplating
Important beters: density: 1.22 g/cm3 notched impact strength: 45 elongation at break: bending strength: 83.33 MPa flexural modulus: 2156.86 MPa hardness: 115
Manufacturer: Korea LG chemical company
PC/ABS (PC and ABS alloy) /HAC8250/ kumhosunny
Usage: other
Features: high impact
Important beters: melt flow rate: 56 g/10min density: 1.13 g/cm3 molding shrinkage rate: 0.6% notched impact strength: 60 tensile strength: 56.86 MPa elongation: 180% bending strength: 76.47 MPa flexural modulus: 2156.86 MPa hardness: 116 VEKA softening point of 116 DEG C heat debation temperature: 106 degrees
Manufacturer: Shanghai kumhosunny Plastics Co., Ltd.
PC/ABS (PC /T-3011/ and ABS alloy) Japan Teijin
Usage: other
Features: good heat resistance and impact resistance
Important beters: density: 1.14 g/cm3 molding shrinkage rate: 0.6% notched impact strength: 80 elongation at break: bending strength: 90 MPa bending modulus: 2500 MPa VEKA softening point: thermal debation temperature: 105 C
Manufacturer: Japan Teijin chemical company
PC/ABS (PC and ABS alloy) /1110/ Shenzhen optimization
Usage: other
Features: environmental protection, high flow, high impact resistance, low density
Important beters: melt flow rate: 20 g/10min density: 1.12 g/cm3 absorption rate: 0.11% molding shrinkage rate: 0.6% notched impact strength: 65 tensile strength: 55 MPa flexural strength: 65 MPa flexural modulus: 2300 MPa hardness: 112 thermal debation temperature: 100 degrees
Shenzhen Engineering Plastics Co., Ltd.
PC/ABS (PC & ABS) /A2200/ Shenzhen Asia Pacific
Usage: other
Features note: high flow, environmentally friendly flame retardant V0.
Important beters: melt flow rate: 25 g/10min density: 1.18 g/cm3 molding shrinkage rate: 0.5% notched impact strength: 45 tensile strength: 57 MPa elongation: 55% bending strength: 89 MPa flexural modulus of 2501 MPa hot debation temperature: 85 degrees
Shenzhen Yatai Industrial Co., Ltd.
ABS/PC (ABS and PC alloy #) /HI-1001BG/ Samsung Cheil
Usage: other
Important beters: melt flow rate: 68 g/10min density: 1.09 g/cm3 absorption rate: 0.2% molding shrinkage rate: 0.5% tensile strength: 48.3 MPa flexural strength: 73.8 MPa flexural modulus: 2140 MPa hardness: 105 VEKA softening point of 105 DEG C heat debation temperature: 92.2 degrees
Manufacturer: Korea first wool weaving Co.