Physical Properties
Metric
English
Comments
Density
1.20 g/cc
0.0434 lb/in3
ISO 1183
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
85
85
ISO 868
Hardness, Shore D
33
33
ISO 868
Tensile Strength
2.00 MPa
@Strain 10.0 %
290 psi
@Strain 10.0 %
200 mm/min; DIN 53504
4.70 MPa
@Strain 50.0 %
682 psi
@Strain 50.0 %
200 mm/min; DIN 53504
5.80 MPa
@Strain 100 %
841 psi
@Strain 100 %
200 mm/min; DIN 53504
16.6 MPa
@Strain 300 %
2410 psi
@Strain 300 %
200 mm/min; DIN 53504
Tensile Strength, Ultimate
52.0 MPa
7540 psi
200 mm/min; DIN 53504
Elongation at Break
531 %
531 %
200 mm/min; DIN 53504
Tensile Modulus
0.0210 GPa
@Temperature 60.0 °C
3.05 ksi
@Temperature 140 °F
storage; ISO 6721-1,-4
其他型号参数与生产商——————————
ABS/PC (ABS and PC alloy #) /AN-312/ India Bhansali
Usage: other
Features: granular material
Important beters: melt flow rate: 50 g/10min density: 1.17 g/cm3 molding shrinkage rate: 0.4% notched impact strength: 196 tensile strength: 39.2 MPa flexural strength: 53.9 MPa flexural modulus: 1770 MPa hardness: 105 VEKA softening point of 98 DEG C heat debation temperature: 88 degrees
Manufacturer: India Bhansali engineering polymer Co., Ltd.
ABS/PC (ABS and PC alloy #) /AN-450/ India Bhansali
Usage: other
Features: granular material
Important beters: melt flow rate: 63 g/10min density: 1.17 g/cm3 molding shrinkage rate: 0.4% notched impact strength: 177 tensile strength: 41.2 MPa flexural strength: 56.9 MPa flexural modulus: 2060 MPa hardness: 106 VEKA softening point of 99 DEG C heat debation temperature: 88 degrees
Manufacturer: India Bhansali engineering polymer Co., Ltd.
ABS/PC (ABS and PC alloy #) /AP8020/ India bulated
Usage: other
Features: good impact resistance, granular material
Important beters: density: 1.12 g/cm3 molding shrinkage rate: 0.5% notched impact strength: tensile strength: 40 MPa elongation at break: 40% bending strength: 85 MPa bending modulus: 2300 MPa thermal debation temperature: 92 C
Manufacturer: India bulated polymer Co., Ltd.
PC/ABS (PC & ABS) /1003/ us Lucent
Usage: other
Important beters: melt flow rate: 3 g/10min density: 1.13 g/cm3 molding shrinkage rate: 0.7% notched impact strength: 534 tensile strength: 53.79 MPa elongation: 120% bending strength: 82.76 MPa flexural modulus of 2275.86 MPa hot debation temperature: 115.56 degrees
Manufacturer: Lucent Polymer Co
ABS/PC (ABS PC and /CP5101F/LG chemical # alloy)
Usage: other
Remarks: the carbon nano filler has good processability
Important beters: melt flow rate: 30 g/10min density: 1.21 g/cm3 molding shrinkage rate: 0.4% tensile strength: MPa bending strength: 98.1 MPa bending modulus: 2840 MPa thermal debation temperature: 88 C
Manufacturer: Korea LG chemical company
ABS/PC (ABS PC and /GN5001RFD/LG chemical # alloy)
Usage: other
Remark: no halogen high impact resistance
Important beters: melt flow rate: 15 g/10min density: 1.18 g/cm3 molding shrinkage rate: 0.4% notched impact strength: 588 tensile strength: 61.3 MPa flexural strength: 95.1 MPa flexural modulus: 2600 MPa VEKA softening point: debation temperature of 97 DEG C heat: 92 degrees
Manufacturer: Korea LG chemical company
ABS/PC (ABS PC and /GP5008A/LG chemical # alloy)
Usage: other
Features: granular material
Important beters: melt flow rate: 2 g/10min density: 1.1 g/cm3 absorption rate: 0.16% molding shrinkage rate: 0.5% notched impact strength: 451 tensile strength: 39.2 MPa elongation: 27% bending strength: 59.8 MPa flexural modulus: 1670 MPa VEKA softening point: debation temperature of 97.7 DEG C heat: 91 degrees
Manufacturer: Korea LG chemical company
PC/ABS (PC and ABS alloy) /5200HF.IM/ Jubilee (Trinseo)
Usage: other
Important beters: melt flow rate: 17 g/10min density: 1.17 g/cm3 molding shrinkage rate: 0.4% tensile strength: 55 MPa elongation: 50% bending strength: 97.9 MPa flexural modulus: 2830 MPa VEKA softening point: debation temperature of 108 DEG C heat: 82.2 degrees
Manufacturer: Sheng Xi Ao (Trinseo) Company
PC/ABS (PC and ABS alloy) /B-270/ Jubilee (Trinseo)
Usage: other
Important beters: melt flow rate: 1.5 g/10min density: 1.21 g/cm3 absorption rate: 0.18% molding shrinkage rate: 0.65% notched impact strength: 110 tensile strength: 59.9 MPa elongation: 100% bending strength: 100 MPa flexural modulus of 3310 MPa hot debation temperature: 134 degrees
Manufacturer: Sheng Xi Ao (Trinseo) Company
PC/ABS (PC and ABS alloy) /2002A/ Guangdong stone
Usage: other
Features: high notch impact strength, high flow perbance, high UV resistance
Important beters: density: 1.23 g/cm3 notched impact strength: 70 elongation at break: bending strength: 65 MPa bending modulus: 2400 MPa thermal debation temperature: 100 C
Manufacturer: Guangdong stone chemical Limited by Share Ltd