Physical Properties
Metric
English
Comments
Density
0.930 g/cc
0.0336 lb/in3
ASTM D792
Viscosity
253000 cP
@Shear Rate 206 1/s,
Temperature 200 °C
253000 cP
@Shear Rate 206 1/s,
Temperature 392 °F
ASTM D3835
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
37
37
extruded sample; 5 sec. delay; ASTM D2240
43
43
injection molded sample; 5 sec. delay; ASTM D2240
Tensile Strength at Break
2.10 MPa
305 psi
Die C; Flow direction; ASTM D412
3.10 MPa
450 psi
Die C; Cross direction; ASTM D412
Elongation at Break
263 %
263 %
Die C; Flow direction; ASTM D412
474 %
474 %
Die C; Cross direction; ASTM D412
100% Modulus
1.00 MPa
145 psi
Die C; Cross direction; ASTM D412
1.30 MPa
189 psi
Die C; Flow direction; ASTM D412
Tear Strength
16.0 kN/m
91.3 pli
Die C; Cross direction; ASTM D624
Compression Set
31 %
31 %
22h/23°C; ASTM D395B
41 %
@Temperature 100 °C
41 %
@Temperature 212 °F
22hr; ASTM D395B
其他型号参数与生产商——————————
PA6 (polycaprolactam # nylon 6) /SXXIC / India
Uses: other
Important beters: density: 1.13 g/cm3 water absorption: 2% molding shrinkage: 1.5% notched impact strength: 49 tensile strength: 65 MPa bending strength: 110 MPa bending modulus: 2500 MPa hardness: 75, hot debation temperature: 70 DEG C
Manufacturer: India SRF company
PA6 (polycaprolactam # nylon 6) /1820 Bk-1/ Technical
Uses: other
Important beters: density: 1.14 g/cm3, notch impact strength: 56, elongation at break: 15% bending strength: 110 MPa bending modulus: 2860 MPa, hot debation temperature: 171 DEG C
Manufacturer: American Technical, Polymer Co
PA6 (polycaprolactam # nylon 6) /SXXIC RED/ SRF in India
Uses: other
Important beters: density: 1.13 g/cm3 water absorption: 2% molding shrinkage: 1.5% notched impact strength: 49 tensile strength: 65 MPa bending strength: 110 MPa bending modulus: 2500 MPa hardness: 75, hot debation temperature: 70 DEG C
Manufacturer: India SRF company
PA6 (polycaprolactam # nylon 6) /SXXIC YELLOW/ SRF in India
Uses: other
Important beters: density: 1.13 g/cm3 water absorption: 2% molding shrinkage: 1.5% notched impact strength: 49 tensile strength: 65 MPa bending strength: 110 MPa bending modulus: 2500 MPa hardness: 75, hot debation temperature: 70 DEG C
Manufacturer: India SRF company
PA6 (polycaprolactam # nylon 6 /GR13/ Omni Plastics)
Uses: other
Important beters: density: 1.21 g/cm3, notch impact strength: 74, elongation at break: 4% bending strength: 228 MPa bending modulus: 5870 MPa, hot debation temperature: 216 DEG C
Manufacturer: American Omni Plastics company
PA6 (polycaprolactam # nylon 6 /GR30/ Omni Plastics)
Uses: other
Important beters: density: 1.37 g/cm3, notch impact strength: 130, elongation at break: 3% bending strength: 269 MPa bending modulus: 9660 MPa, hot debation temperature: 218 DEG C
Manufacturer: American Omni Plastics company
PA6 (polycaprolactam # nylon 6 /GR33/ Omni Plastics)
Uses: other
Important beters: density: 1.38 g/cm3, notch impact strength: 130, elongation at break: 3% bending strength: 276 MPa bending modulus: 9660 MPa, hot debation temperature: 218 DEG C
Manufacturer: American Omni Plastics company
PA6 (polycaprolactam # nylon 6 /GR43/ Omni Plastics)
Uses: other
Important beters: density: 1.48 g/cm3, notch impact strength: 140, elongation at break: 3% bending strength: 303 MPa bending modulus: 11700 MPa, hot debation temperature: 218 DEG C
Manufacturer: American Omni Plastics company
PA6 (polycaprolactam # nylon 6 /GR50/ Omni Plastics)
Uses: other
Important beters: density: 1.56 g/cm3, notch impact strength: 140, elongation at break: 3% bending strength: 314 MPa bending modulus: 13800 MPa, hot debation temperature: 218 DEG C
Manufacturer: American Omni Plastics company