Physical Properties
Metric
English
Comments
Density
0.930 g/cc
0.0336 lb/in3
ASTM D792
Viscosity
253000 cP
@Shear Rate 206 1/s,
Temperature 200 °C
253000 cP
@Shear Rate 206 1/s,
Temperature 392 °F
ASTM D3835
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
37
37
extruded sample; 5 sec. delay; ASTM D2240
43
43
injection molded sample; 5 sec. delay; ASTM D2240
Tensile Strength at Break
2.10 MPa
305 psi
Die C; Flow direction; ASTM D412
3.10 MPa
450 psi
Die C; Cross direction; ASTM D412
Elongation at Break
263 %
263 %
Die C; Flow direction; ASTM D412
474 %
474 %
Die C; Cross direction; ASTM D412
100% Modulus
1.00 MPa
145 psi
Die C; Cross direction; ASTM D412
1.30 MPa
189 psi
Die C; Flow direction; ASTM D412
Tear Strength
16.0 kN/m
91.3 pli
Die C; Cross direction; ASTM D624
Compression Set
31 %
31 %
22h/23°C; ASTM D395B
41 %
@Temperature 100 °C
41 %
@Temperature 212 °F
22hr; ASTM D395B
其他型号参数与生产商——————————
PA6 (polycaprolactam # nylon 6) /CM1023G1000/ Japan Dongli
Uses: other
Characteristic note: wear resistance
Important beters: density: 1.13 g/cm3, water absorption: 1.8% tensile strength: 75 MPa, elongation at break: 15% bending strength: 105 MPa bending modulus: 2800 MPa hardness: 119, hot debation temperature: 180 DEG C
Manufacturer: Dongli Industry Co., Ltd.
PA6 (polycaprolactam # nylon 6) /F6040LG/ Ningbo Pu
Uses: other
Characteristic note: long glass fiber reinforced
Important beters: density: 1.49 g/cm3 molding shrinkage rate: 28% notched impact strength: 300 tensile strength: 180 MPa elongation: 3% bending strength: 260 MPa flexural modulus of 9780 MPa thermal debation temperature of 200 DEG C: filler content: 40%
Ningbo golden PU high polymer material Co., Ltd.
PA6 (polycaprolactam # nylon 6 /G30T NC201/ kuibyshevazot)
Uses: other
Characteristic note: 30% short glass fiber reinforced toughening
Important beter:
Manufacturer: Russian kuibyshevazot company
PA6 (polycaprolactam # nylon 6) /HL-G30/ Yuyao Manulife
Uses: other
Characteristic note: 30% glass fiber reinforced, high strength, flame retardant
Important beters: density: 1.35 g/cm3 molding shrinkage: 0.3% tensile strength: 145 MPa, elongation at break: 3% bending strength: 230 MPa bending modulus: 6500 MPa, hot debation temperature: 200 DEG C
Manufacturer: Yuyao Hongli Plastics & Chemical Co., Ltd.
PA6 (polycaprolactam # Fengshan nylon /02GF01/ nylon 6)
Uses: other
Characteristic note: excellent strength and toughness and low temperature resistance
Important beters: melt flow rate: 3.6 g/10min density: 1.22 g/cm3 notched impact strength: 325 tensile strength: 125 MPa bending modulus: 7600 MPa, hot debation temperature: 198 DEG C
Manufacturer: Yuyao Fengshan nylon new material factory
PA6 (polycaprolactam # nylon 6) /N252/ MITSUBISHI engineering plastics
Uses: other
Important beters: density: 1.72 g/cm3 water absorption: 0.24% molding shrinkage: 0.45% bending strength: 241 MPa bending modulus: 20600 MPa hardness: 101, hot debation temperature: 224 DEG C, filler content: 25%
Manufacturer: Japan MITSUBISHI Engineering Plastics Corporation
PA6 (polycaprolactam # nylon 6 /B1303/ Nanjing Hongrui)
Uses: other
Remark: flame retardant and flame retardant.
Important beters: density: 1.3 g/cm3 molding shrinkage: 0.002% notched impact strength: 8 tensile strength: 90 MPa, elongation at break: 3% bending strength: 105 MPa bending modulus: 4500 MPa hardness: 120, hot debation temperature: 195 DEG C
Manufacturer: Nanjing Hongrui Engineering Plastics Co. Ltd.
PA6 (polycaprolactam # nylon 6) /126F5/ Austria SAX
Uses: other
Important beters: density: 1.3 g/cm3 notched impact strength: 10 tensile strength: 160 MPa, elongation at break: 4% bending strength: 265 MPa bending modulus: 6500 MPa VEKA softening point: 214 DEG C hot debation temperature: 209 DEG C
Manufacturer: Austria SAX polymer industry company
PA6 (polycaprolactam # nylon 6) /H3CW (Cond) / BASF
Uses: other
Characteristic note: good heat resistance
Important beters: notched impact strength: 25 tensile strength: 45 MPa bending modulus: 25 MPa
Manufacturer: German Basf Inc
PA6 (polycaprolactam # nylon 6) /AN0720SB/ Jin Lun Technology
Uses: other
Characteristic note: high heat resistance, high rigidity
Important beters: density: 1.41 g/cm3 absorption rate: 1% molding shrinkage rate: 0.3% notched impact strength: 96.1 tensile strength: 145 MPa elongation: 1.9% bending strength: 200 MPa flexural modulus: 8270 MPa hardness: 120 thermal debation temperature: 205 degrees
Manufacturer: Jin Lun Polytron Technologies Inc