Physical Properties
Metric
English
Comments
Density
0.930 g/cc
0.0336 lb/in3
ASTM D792
Viscosity
253000 cP
@Shear Rate 206 1/s,
Temperature 200 °C
253000 cP
@Shear Rate 206 1/s,
Temperature 392 °F
ASTM D3835
Mechanical Properties
Metric
English
Comments
Hardness, Shore A
37
37
extruded sample; 5 sec. delay; ASTM D2240
43
43
injection molded sample; 5 sec. delay; ASTM D2240
Tensile Strength at Break
2.10 MPa
305 psi
Die C; Flow direction; ASTM D412
3.10 MPa
450 psi
Die C; Cross direction; ASTM D412
Elongation at Break
263 %
263 %
Die C; Flow direction; ASTM D412
474 %
474 %
Die C; Cross direction; ASTM D412
100% Modulus
1.00 MPa
145 psi
Die C; Cross direction; ASTM D412
1.30 MPa
189 psi
Die C; Flow direction; ASTM D412
Tear Strength
16.0 kN/m
91.3 pli
Die C; Cross direction; ASTM D624
Compression Set
31 %
31 %
22h/23°C; ASTM D395B
41 %
@Temperature 100 °C
41 %
@Temperature 212 °F
22hr; ASTM D395B
其他型号参数与生产商——————————
PA6 (polycaprolactam # nylon 6) /UGN16080MF/ Korea koplar
Uses: other
Characteristic note: GF60 high rigidity, surface improvement
Important beters: density: 1.72 g/cm3 water absorption: 0.8% molding shrinkage: 0.1% tensile strength: 2150 MPa bending strength: 3100 MPa bending modulus: 165000 MPa hardness: 122, hot debation temperature: 218 DEG C
Manufacturer: South Korea koplar Engineering Plastics Co. Ltd.
PA6 (polycaprolactam # nylon 6) /GF15 FR-N/ TPC
Uses: other
Important beters: density: 1.26 g/cm3 absorption rate: 1.4% molding shrinkage rate: 0.7% notched impact strength: 53.4 tensile strength: 96.5 MPa elongation: 4% bending strength: 145 MPa flexural modulus: 3100 MPa hardness: 120 thermal debation temperature: 196 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF25 L BK/ TPC
Uses: other
Remark: granule material
Important beters: density: 1.23 g/cm3 absorption rate: 0.9% molding shrinkage rate: 0.5% notched impact strength: 69.4 tensile strength: 191 MPa elongation: 3% bending strength: 290 MPa flexural modulus: 10300 MPa hardness: 115 thermal debation temperature: 213 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /E HS N/ TPC
Uses: other
Characteristic note: stability, nub
Important beters: density: 1.13 g/cm3 absorption rate: 1.6% molding shrinkage rate: 1.2% notched impact strength: 133 tensile strength: 80 MPa elongation: 90% bending strength: 117 MPa flexural modulus: 3100 MPa hardness: 100 thermal debation temperature: 76.7 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GB15 L BK/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.24 g/cm3 absorption rate: 1.1% molding shrinkage rate: 1.7% notched impact strength: 37.4 tensile strength: 68.9 MPa elongation: 3.5% bending strength: 276 MPa flexural modulus: 12600 MPa hardness: 119 thermal debation temperature: 138 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF20 L BK001/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.3 g/cm3 absorption rate: 1.4% molding shrinkage rate: 0.4% notched impact strength: 74.7 tensile strength: 131 MPa elongation: 3.5% bending strength: 200 MPa flexural modulus: 6890 MPa hardness: 115 thermal debation temperature: 204 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L BK001/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L NAT024/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L RD041/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company
PA6 (polycaprolactam # nylon 6) /GF33 L RD079/ TPC
Uses: other
Characteristic note: Lubrication
Important beters: density: 1.37 g/cm3 absorption rate: 1.3% molding shrinkage rate: 0.3% notched impact strength: 117 tensile strength: 165 MPa elongation: 2.5% bending strength: 255 MPa flexural modulus: 8620 MPa hardness: 118 thermal debation temperature: 210 degrees
Manufacturer: American TP Composites company