Physical Properties
Metric
English
Comments
Specific Gravity
1.07 g/cc
1.07 g/cc
ASTM D792
Maximum Moisture Content
0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow
0.0040 - 0.0070 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0070 in/in
@Thickness 0.126 in
ASTM D955
Melt Flow
30 g/10 min
@Load 10.0 kg,
Temperature 220 °C
30 g/10 min
@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties
Metric
English
Comments
Hardness, Rockwell R
98
98
ASTM D785
Tensile Strength, Yield
43.1 MPa
@Thickness 3.20 mm
6260 psi
@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Break
>= 10 %
@Thickness 3.20 mm
>= 10 %
@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Yield
>= 5.0 %
@Thickness 3.20 mm
>= 5.0 %
@Thickness 0.126 in
50 mm/min; ASTM D638
Tensile Modulus
1.66 GPa
@Thickness 3.20 mm
240 ksi
@Thickness 0.126 in
1 mm/min; ASTM D638
Flexural Yield Strength
69.6 MPa
@Thickness 3.20 mm
10100 psi
@Thickness 0.126 in
15 mm/min; ASTM D790
Flexural Modulus
2.16 GPa
@Thickness 3.20 mm
313 ksi
@Thickness 0.126 in
15 mm/min; ASTM D790
Izod Impact, Notched
4.90 J/cm
@Thickness 3.20 mm
9.18 ft-lb/in
@Thickness 0.126 in
ASTM D256
其他型号参数与生产商——————————
ABS (acrylonitrile / butadiene / styrene copolymer #) /EX18A/ Japan UMG
Uses: other
Important beters: melt flow rate: 18 g/10min notched impact strength: 13 bending modulus: 2650 MPa, hot debation temperature: 83 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /EX10U/ Japan UMG
Uses: other
Important beters: melt flow rate: 14 g/10min notched impact strength: 25 bending modulus: 2400 MPa, hot debation temperature: 79 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /EX19C/ Japan UMG
Uses: other
Important beters: melt flow rate: 55 g/10min notched impact strength: 14 bending modulus: 2450 MPa, hot debation temperature: 79 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /TW15F/ Japan UMG
Uses: other
Important beters: melt flow rate: 5 g/10min notched impact strength: 11 bending modulus: 2300 MPa, hot debation temperature: 92 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /TW20B/ Japan UMG
Uses: other
Important beters: melt flow rate: 5 g/10min notched impact strength: 12 bending modulus: 2350 MPa, hot debation temperature: 94 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /UT20B/ Japan UMG
Uses: other
Important beters: melt flow rate: 2 g/10min notched impact strength: 11 bending modulus: 2700 MPa, hot debation temperature: 95 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /UT30B/ Japan UMG
Uses: other
Important beters: melt flow rate: 6 g/10min notched impact strength: 9 bending modulus: 2850 MPa, hot debation temperature: 95 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /EX47E/ Japan UMG
Uses: other
Important beters: melt flow rate: 2 g/10min notched impact strength: 15 bending modulus: 2150 MPa, hot debation temperature: 95 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /VW7/ Japan UMG
Uses: other
Important beters: melt flow rate: 35 g/10min notched impact strength: 12 bending modulus: 2600 MPa, hot debation temperature: 74 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /VW55J/ Japan UMG
Uses: other
Important beters: melt flow rate: 26 g/10min notched impact strength: 14 bending modulus: 2550 MPa, hot debation temperature: 74 DEG C
Manufacturer: Japan UMG ABS Co., Ltd.