Physical Properties
Metric
English
Comments
Specific Gravity
1.07 g/cc
1.07 g/cc
ASTM D792
Maximum Moisture Content
0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow
0.0040 - 0.0070 cm/cm
@Thickness 3.20 mm
0.0040 - 0.0070 in/in
@Thickness 0.126 in
ASTM D955
Melt Flow
30 g/10 min
@Load 10.0 kg,
Temperature 220 °C
30 g/10 min
@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties
Metric
English
Comments
Hardness, Rockwell R
98
98
ASTM D785
Tensile Strength, Yield
43.1 MPa
@Thickness 3.20 mm
6260 psi
@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Break
>= 10 %
@Thickness 3.20 mm
>= 10 %
@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Yield
>= 5.0 %
@Thickness 3.20 mm
>= 5.0 %
@Thickness 0.126 in
50 mm/min; ASTM D638
Tensile Modulus
1.66 GPa
@Thickness 3.20 mm
240 ksi
@Thickness 0.126 in
1 mm/min; ASTM D638
Flexural Yield Strength
69.6 MPa
@Thickness 3.20 mm
10100 psi
@Thickness 0.126 in
15 mm/min; ASTM D790
Flexural Modulus
2.16 GPa
@Thickness 3.20 mm
313 ksi
@Thickness 0.126 in
15 mm/min; ASTM D790
Izod Impact, Notched
4.90 J/cm
@Thickness 3.20 mm
9.18 ft-lb/in
@Thickness 0.126 in
ASTM D256
其他型号参数与生产商——————————
ABS (acrylonitrile / butadiene / styrene copolymer #) /H702/ ABS
Uses: other
Characteristic note: good flow, medium heat resistance
Important beters: melt flow rate: 16 g/10min density: 1.04 g/cm3 molding shrinkage rate: 0.55% notched impact strength: 17 bending strength: 73 MPa flexural modulus: 2450 MPa hardness: 105 VEKA softening point of 104 DEG C heat debation temperature: 99 degrees
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /H802/ ABS
Uses: other
Characteristic note: good flow and high heat resistance
Important beters: density: 1.05 g/cm3 molding shrinkage: 0.55% notched impact strength: 15 bending strength: 80 MPa bending modulus: 2700 MPa VEKA softening point: 109 degrees of hot debation temperature: 101 DEG C
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /M305/ ABS
Uses: other
Features: good dimensional stability
Important beters: melt flow rate: 12 g/10min density: 1.05 g/cm3 molding shrinkage rate: 0.65% notched impact strength: 21 bending strength: 68 MPa flexural modulus: 2300 MPa hardness: 95 VEKA softening point of 99 DEG C heat debation temperature: 94 degrees
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /SAN ABS 51/
Uses: other
Important beters: melt flow rate: 15 g/10min density: 1.08 g/cm3 molding shrinkage rate: 0.35% notched impact strength and elongation at break: 2: 3.8%: 125 MPa flexural strength flexural modulus: 3900 MPa hardness: 126 VEKA softening point of 106 DEG C heat debation temperature of 102 DEG C: light transmittance: 87.5%
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer # fuyuda plasticizing) /ABS-F1/
Uses: other
Note: the characteristics of using high perbance composite flame retardant modified ABS flame retardant flame retardant has good flame retardant perbance, add less features, in addition to maintaining ABS high strength and high modulus, excellent surface gloss and other properties, but also improve the processability of ABS.
Important beters: melt flow rate: 3.5 g/10min density: 1.165 g/cm3 notched impact strength: 60 tensile strength: 55 MPa, elongation at break: 25% bending strength: 80 MPa bending modulus: 2500 MPa, hot debation temperature: 78 DEG C
Manufacturer: Cixi Da Da plasticization Co., Ltd.
ABS (acrylonitrile / butadiene / styrene copolymer #) /633/ ABS
Uses: other
Characteristic note: 633 resin is a universal injection molding ABS resin (acrylonitrile, butadiene, styrene). High gloss and good fluidity
Important beters: melt flow rate: 15 g/10min density: 1.05 g/cm3 molding shrinkage rate: 0.5% notched impact strength: 347 tensile strength: 41.3 MPa flexural strength: 65.5 MPa flexural modulus: 2200 MPa hardness: 109 VEKA softening point of 106 DEG C heat debation temperature: 85 degrees
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /451/ ABS
Uses: other
Remark: medium gloss, medium heat resistance, medium impact resistance
Important beters: melt flow rate: 7 g/10min density: 1.07 g/cm3 molding shrinkage rate: 0.5% notched impact strength: 176 tensile strength: 43.4 MPa flexural strength: 72.4 MPa flexural modulus: 2690 MPa hardness: 113 thermal debation temperature: 85 degrees
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /E112LG/ ABS
Uses: other
Characteristic note: low gloss
Important beters: melt flow rate: 6 g/10min density: 1.04 g/cm3 molding shrinkage rate: 0.65% notched impact strength: 8 bending strength: 43 MPa flexural modulus: 1500 MPa hardness: 65 VEKA softening point of 98 DEG C heat debation temperature: 95 degrees
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /P2L-AT/ ABS
Uses: other
Important beters: melt flow rate: 45 g/10min density: 1.05 g/cm3 notched impact strength: 10 VEKA softening point: 96 degrees of hot debation temperature: 92 degrees centigrade
Manufacturer: Ineos ABS company
ABS (acrylonitrile / butadiene / styrene copolymer #) /H605/ ABS
Uses: other
Characteristic note: good flow and high heat resistance
Important beters: melt flow rate: 25 g/10min density: 1.05 g/cm3 molding shrinkage rate: 0.5% notched impact strength: 17 bending strength: 72 MPa flexural modulus: 2400 MPa hardness: 105 VEKA softening point of 101 DEG C heat debation temperature: 98 degrees
Manufacturer: Ineos ABS company