产品详情
项目
测试条件
属性值
单位
测试方法
物理性能 |
||||
| 熔指(MFR) | 载荷 5.0kg,temperature 280℃ |
|
g/10 min | ASTM D1238 |
| 吸湿性 |
|
% | ASTM D570 | |
| 密度 |
|
无 | ASTM D792 | |
| 收缩率 | 横向 |
|
cm/cm | SABIC Method |
| 收缩率 | 流动，thickness 3.2mm |
|
cm/cm | SABIC Method |
机械性能 |
||||
| 拉伸屈服强度 | type I，50mm/min |
|
MPa | ASTM D638 |
| 洛氏硬度 | R级 |
|
无 | ASTM D785 |
| 拉伸模量 | 5mm/min |
|
GPa | ASTM D638 |
| 拉伸模量 | 1mm/min |
|
GPa | ISO 527 |
| 弯曲模量 |
|
GPa | ISO 178 | |
| 弯曲模量 | 2.6mm/min,100mm span |
|
GPa | ASTM D790 |
| 弯曲模量 | 1.3mm/min,50mm span |
|
GPa | ASTM D790 |
| 落锤冲击 | temperature 23℃ |
|
J | ASTM D3763 |
| 屈服伸长率 | type I，50mm/min |
|
% | ASTM D638 |
| 屈服伸长率 |
|
% | ISO 527 | |
| 拉伸断裂强度 | type I，50mm/min |
|
MPa | ASTM D638 |
| 拉伸断裂强度 |
|
MPa | ISO 527 | |
| 拉伸断裂强度 |
|
MPa | ISO 527 | |
| 悬臂梁缺口冲击强度 | temperature -300℃ |
|
J/cm | ASTM D256 |
| 悬臂梁缺口冲击强度 | 80*10*4 |
|
kJ/m² | ISO 180/1A |
| 悬臂梁缺口冲击强度 |
|
J/cm | ASTM D256 | |
| 断裂伸长率 | type I，50mm/min |
|
% | ASTM D638 |
| 断裂伸长率 |
|
% | ISO 527 | |
| 弯曲强度 | 1.3mm/min,50mm span |
|
MPa | ASTM D790 |
| 弯曲强度 |
|
MPa | ISO 178 | |
| 弯曲强度 | 2.6mm/min,100mm span |
|
MPa | ASTM D790 |
热性能 |
||||
| 载荷下热变形温度 | 1.8mpa |
|
°C | ISO 75/Ae |
| 载荷下热变形温度 | 0.46mpa |
|
°C | ISO 75/Be |
| 载荷下热变形温度 | 1.8mpa,thickness 6.4mm |
|
°C | ASTM D648 |
| 载荷下热变形温度 | 1.8mpa,thickness 3.2mm |
|
°C | ASTM D648 |
| 载荷下热变形温度 | 0.46mpa |
|
°C | ASTM D648 |
| 维卡软化点 |
|
°C | ISO 306 | |
| 维卡软化点 |
|
°C | ISO 306 | |
电气性能 |
||||
| 介电强度 | thickness 3.2mm |
|
kV/mm | ASTM D149 |
| 高电弧燃烧指数 |
|
无 | UL 746A | |
| 表面电阻率 |
|
ohms | ASTM D257 | |
| 介电常数 | frequency 50.0-60.0 hz |
|
无 | ASTM D150 |
| 介电常数 | frequency 1.00e+6 hz |
|
无 | ASTM D150 |
| 相对漏电起痕指数 |
|
V | UL 746A | |
| 耗散因数 | frequency 50.0-60.0 hz |
|
无 | ASTM D150 |
| 耗散因数 | frequency 1.00e+6 hz |
|
无 | ASTM D150 |
| 耐电弧性 |
|
sec | ASTM D495 | |
| 体积电阻率 |
|
ohms·cm | ASTM D257 | |
阻燃性能 |
||||
| 阻燃等级 | thickness 1.47mm |
|
无 | UL 94 |
其它性能 |
||||
| 热丝引燃 (HWI) |
|
sec | UL 746A | |
| 相对温度指数 |
|
°C | UL 746B | |
| 相对温度指数 | 机械无冲击 |
|
°C | UL 746B |
| 相对温度指数 | 机械冲击 |
|
°C | UL 746B |