| 牌号：W18Cr4VCo5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 标准：GB/T9943-1988 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| ●特性及适用范围： |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 为钨系一般含钴型高速钢，较W18Cr4V的红硬性和高温硬度稍高，但韧性低，淬火后，表面硬度可达63～66HRC。用作高速切削刀具、自动化机床的刀具，供切削较高强度材料用。 |
| ●化学成份： |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 碳C：0.70～0.80(允许偏差:±0.01) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 硅Si：0.20～0.40(允许偏差:±0.05) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 锰Mn：0.10～0.40(允许偏差:+0.04) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 硫S：≤0.030 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 磷P：≤0.030 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 铬Cr：3.75～4.50(允许偏差:±0.05) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 镍Ni：允许残余含量≤0.30 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 铜Cu：允许残余含量≤0.25 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 钒V：0.80～1.20(允许偏差:±0.05) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 钼Mo：0.40～1.00(允许偏差:尺寸≤6,±0.05;尺寸＞6,±0.10) |
|
|
|
|
|
|
|
|
|
|
|
|
| 钨W：17.50～19.00(允许偏差:尺寸≤10,±0.10;尺寸＞10,±0.20) |
|
|
|
|
|
|
|
|
|
|
|
|
| 钴Co：4.25～5.75(允许偏差:±0.15) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| ●力学性能： |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 硬度：交货硬度:(其他加工方法)≤285HB;(退火)≤269HB。试样热处理制度及淬回火硬度:≥63HRC |
|
|
|
|
|
|
|
|
| ●热处理规范及金相组织： |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 热处理规范：淬火,820～870℃预热，1270～1290℃(盐浴炉)或1280～1300℃(箱式炉)加热，油冷，540～560℃回火2次，每次2h。 |
|
|
|
|
|
|
| ●交货状态：热轧、锻制、冷拉钢棒以退火状态交货，热轧、锻制钢棒以退火＋其他加工方法（剥皮、轻拉、磨光或抛光等）加工后交货 |