产品详情
LEXAN™
124R resin
聚碳酸酯
产品说明:
LEXAN 124R is a low viscosity multi purpose grade. FDA food contact
compliant in limited colors. Effective January 15th, 2007 this grade is no
longer supported with biocompatibility inbation and should not be used for
medical applications which require biocompatibility. Contact your GE
representative for the alternative grade in the LEXAN HP
series.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
||||
|
UL 黄卡 2
|
||||
|
搜索 UL
黄卡
|
|
|||
|
供货地区
|
|
|||
|
特性
|
|
|||
|
用途
|
|
|||
|
机构评级
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
ASTM D792 | ||
|
--
|
1.20
|
g/cm³
|
|
|
--
|
1.19
|
g/cm³
|
|
|
特定体积
|
0.835
|
cm³/g
|
ASTM D792 |
|
熔流率（熔体流动速率） (300°C/1.2
kg)
|
18
|
g/10 min
|
ASTM D1238 |
|
收缩率 - 流动 (3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
|
吸水率
|
ASTM D570 | ||
|
24
hr
|
0.15
|
%
|
|
|
平衡,
23°C
|
0.35
|
%
|
|
|
平衡,
100°C
|
0.58
|
%
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
洛氏硬度
|
ASTM D785 | ||
|
M
级
|
70
|
|
|
|
R
级
|
118
|
|
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度 3
|
ASTM D638 | ||
|
屈服
|
62.1
|
MPa
|
|
|
断裂
|
68.9
|
MPa
|
|
|
伸长率 3
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
断裂
|
130
|
%
|
|
|
弯曲模量 4 (50.0 mm 跨距)
|
2340
|
MPa
|
ASTM D790 |
|
弯曲强度 4 (屈服, 50.0 mm
跨距)
|
96.5
|
MPa
|
ASTM D790 |
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
转轮)
|
10.0
|
mg
|
ASTM D1044 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C)
|
690
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击 (23°C)
|
3200
|
J/m
|
ASTM D4812 |
|
落锤冲击 (23°C)
|
169
|
J
|
ASTM D3029 |
|
拉伸冲击强度 5
|
546
|
kJ/m²
|
ASTM D1822 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa,
未退火, 6.40 mm
|
138
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
129
|
°C
|
|
|
维卡软化温度
|
154
|
°C
|
ASTM D1525 6 |
|
线形热膨胀系数 - 流动 (-40 到 95°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
|
比热
|
1260
|
J/kg/°C
|
ASTM C351 |
|
导热系数
|
0.19
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
130
|
°C
|
UL 746 |
|
RTI Imp
|
130
|
°C
|
UL 746 |
|
RTI
|
130
|
°C
|
UL 746 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
> 1.0E+17
|
ohm·cm
|
ASTM D257 |
|
介电强度 (3.20 mm, in
Air)
|
15
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
50
Hz
|
3.17
|
|
|
|
60
Hz
|
3.17
|
|
|
|
1
MHz
|
2.96
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
50
Hz
|
9.0E-4
|
|
|
|
60
Hz
|
9.0E-4
|
|
|
|
1
MHz
|
0.010
|
|
|
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746 |
|
高电弧燃烧指数(HAI)
|
PLC 1
|
|
UL 746 |
|
高电压电弧起痕速率 (HVTR)
|
PLC 2
|
|
UL 746 |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.47 mm)
|
HB
|
|
UL 94 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
折射率
|
1.586
|
|
ASTM D542 |
|
透射率 (2540 µm)
|
88.0
|
%
|
ASTM D1003 |
|
雾度 (2540
µm)
|
1.0
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
260 到 282
|
°C
|
|
|
料筒中部温度
|
271 到 293
|
°C
|
|
|
料筒前部温度
|
282 到 304
|
°C
|
|
|
射嘴温度
|
277 到 299
|
°C
|
|
|
加工（熔体）温度
|
282 到 304
|
°C
|
|
|
模具温度
|
71.0 到 93.0
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|