牌号
|
TStE355低合金结构钢热轧钢板
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
中国ISC
|
L03455
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
对应标准
|
GB /T 3274-2017
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
碳素结构钢和低合金结构钢热轧钢板和钢带
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Hot-rolled plates, sheets and strips of carbon structural steels and high strength low alloy structural sheets
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
品牌/供货源
|
中国大陆-> 宝钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
归类
|
合金钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
性能
|
低温韧性 易切削性 焊接性
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
标签
|
热轧钢板和钢带 低合金结构钢
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
说明
|
性能特点：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
综合力学性能好，冷热加工性能、焊接性能和耐蚀性能均好;具有良好的低温韧性。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
用途举例：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
广泛应用于桥梁、车辆、船舶、建筑、压力容器等。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
本标准适用于厚度不大于400mm的碳素结构钢和低合金钢热轧钢板和钢带
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TStE355化学元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Cu
|
Mo
|
N
|
Ti
|
V
|
Nb
|
Al b
|
|
最小值
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.015
|
|
最大值
|
0.18
|
0.5
|
1.7
|
0.025
|
0.02
|
0.3
|
0.5
|
0.3
|
0.1
|
0.012
|
0.2
|
0.15
|
0.07
|
-
|
|
钢的牌号和化学成分(熔炼分析)应符合GB/T 700和GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
b当采用全铝（Al<sub>t</sub>）含量表示时，Al<sub>t</sub>应不小于0.02%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
TStE355机械性能
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
厚度(直径，边长）
|
抗拉强度
|
屈服点
|
断后伸长率或延伸率
|
|
|
|
|
|
|
|
|
|
|
|
|
t
|
σb
|
σs
|
δ
|
|
|
|
|
|
|
|
|
|
|
|
|
mm
|
Mpa
|
Mpa
|
%
|
|
|
|
|
|
|
|
|
|
|
|
|
t≤16
|
470~630
|
≥345
|
≥21
|
|
|
|
|
|
|
|
|
|
|
|
|
16<t≤40
|
470~630
|
≥335
|
≥21
|
|
|
|
|
|
|
|
|
|
|
|
|
40＜t≤63
|
470~630
|
≥325
|
≥20
|
|
|
|
|
|
|
|
|
|
|
|
|
63＜t≤80
|
470~630
|
≥315
|
≥20
|
|
|
|
|
|
|
|
|
|
|
|
|
80＜t≤100
|
470~630
|
≥305
|
≥20
|
|
|
|
|
|
|
|
|
|
|
|
|
100＜t≤150
|
450~600
|
≥285
|
≥19
|
|
|
|
|
|
|
|
|
|
|
|
|
150＜t≤200
|
450~600
|
≥275
|
≥18
|
|
|
|
|
|
|
|
|
|
|
|
|
200＜t≤250
|
450~600
|
≥265
|
≥18
|
|
|
|
|
|
|
|
|
|
|
|
|
250＜t≤400
|
450~600
|
≥265
|
≥17
|
|
|
|
|
|
|
|
|
|
|
|
|
1、力学性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
①厚度小于3mm的钢板和钢带的抗拉强度和断后伸长率应符合GB/T 700、GB/T 1591的规定，断后伸长率允许比GB/T 700或GB/T 1591的规定降低5%(绝对值)。根据需方要求，钢板和钢带的屈服强度可按GB/T 700、GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
②厚度不小于3mm的钢板和钢带的力学和工艺性能应符合GB/T 700、GB/T 1591的规定。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
2、工艺性能：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
钢板和钢带应做180°弯曲试验，试样弯曲压头直径应符合GB/T 700、GB/T 1591的规定。如供方能保证冷弯试验合格，可不作检验。
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|